多孔質紡錘状構造とその応用リチウムイオン電池のための無水ふっ化鉄の調製【Powered by NICT】

Preparation of anhydrous iron fluoride with porous fusiform structure and its application for Li-ion batteries

著者 (6件)： Sun Hongxu (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Zhou Haochen (Department of Aerospace, Tsinghua University, Beijing, 100084, China) ,  Xu Zhanglin (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Ding Jing (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Yang Juan (School of Metallurgy and Environment, Central South University, Changsha 410083, China) ,  Zhou Xiangyang (School of Metallurgy and Environment, Central South University, Changsha 410083, China)
資料名： Microporous and Mesoporous Materials  (Microporous and Mesoporous Materials)
巻： 253  ページ： 10-17  発行年： 2017年 
JST資料番号： E0642C  ISSN： 1387-1811  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ふっ化鉄はリチウムイオン電池のカソード材料として高い比容量のための研究者の注目を集めている。本研究では,電気化学的性能を改善するためのフッ化鉄の構造調整に焦点を当て自身,であった。紡錘状構造を有する一種の多孔質FeF_3のを容易なソルボサーマル法とその後の熱処理により合成した。水和FeF_3の合成過程は簡単で経済的な原料(絶対エチルアルコール中の鉄塩とHF)を用いて行った。結晶水は大気中で穏やかな乾燥によって除去され,空孔度が遅い脱水プロセスを通して与えた。電気化学的性能は,合成したままの多孔質FeF_3は20mA g~( 1)で100サイクルで137.3mA g~( 1)の安定した可逆容量を実現できることを示した。比容量はフッ化鉄の現在の研究結果の中等度であるが,この開放多孔質構造はフッ化鉄のサイクル安定性を明らかに増強して,更なる処理により著しく改善されることが期待される。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *リチウムイオン電池 ,  *鉄 ,  *多孔性 ,  結晶水 ,  熱処理 ,  *楕円体 ,  脱水 ,  水和
準シソーラス用語： 多孔構造 ,  可逆容量 ,  ソルボサーマル合成 ,  電気化学的性能 ,  比容量 ,  カソード材料【電池】 ,  *フッ化鉄 , 【Automatic Indexing@JST】

著者キーワード (5件)： カソード材料 ,  ふっ化鉄 ,  多孔質構造 ,  熱処理 ,  電気化学的性能