溶接したままおよび熱処理した条件でのレーザ溶接高強度Mg-Gd-Y-Zr合金の高温引張特性

High temperature tensile properties of laser-welded high-strength Mg-Gd-Y-Zr alloy in as-welded and heat-treated conditions

著者 (9件)： WANG Lyuyuan (Shanghai Jiao Tong Univ., Shanghai, CHN) ,  WANG Lyuyuan (Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, CHN) ,  HUANG Jian (Shanghai Jiao Tong Univ., Shanghai, CHN) ,  HUANG Jian (Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, CHN) ,  DONG Jie (Shanghai Jiao Tong Univ., Shanghai, CHN) ,  LI Zhuguo (Shanghai Jiao Tong Univ., Shanghai, CHN) ,  LI Zhuguo (Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, CHN) ,  WU Yixiong (Shanghai Jiao Tong Univ., Shanghai, CHN) ,  WU Yixiong (Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, CHN)
資料名： Welding in the World  (Welding in the World)
巻： 61  号： 2  ページ： 299-306  発行年： 2017年03月 
JST資料番号： H0722A  ISSN： 0043-2288  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 航空機や自動車の軽量化にマグネシウム合金の利用は魅力的で,欠点であった高温強度もGdを添加することで大幅な改善が見られた。さらなる機械的性質の向上の要求に対して,Mg-Gd-Y-ZR合金が開発された。しかしながら,その利用の上で必要となる溶接においては熱影響部および部分融解部での強度要因である析出物の再溶解が起こり,強度の低下が生じる問題が指摘されている。本研究においては,この課題に対する解としての溶接後熱処理(PWHT)の効果を調べた。Mg-Gd-Y-Zr合金の4mm厚板をファイバーレーザを用いて溶接しサンプルを調製した。サンプルの一部についてPWHT(溶体化,水焼入れ,および時効)を実施した。サンプルの金属組織観察および引張試験を実施した。これらの実験から,PWHTは顕著にこの合金の溶接部の高温強度を高めることを確認した。しかしながら,この合金は200°Cを超えるとその機械的性質は急激に低下することも明らかにした。

シソーラス用語： *マグネシウム合金 ,  ガドリニウム含有合金 ,  イットリウム含有合金 ,  ジルコニウム含有合金 ,  レーザ溶接 ,  *溶接熱影響部 ,  *焼なまし ,  高温強さ ,  時効
準シソーラス用語： *溶接後熱処理

分類 (2件)： 溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (6件)： 溶接 ,  熱処理 ,  レーザ溶接 ,  高強度 ,  Mg-Gd-Y-Zr合金 ,  引張特性