文献

J-GLOBAL ID：201702276642920960   整理番号：17A0407518

模擬太陽光下での強化された光触媒活性を有するウニ状FeドープSnO_2のワンポット合成【Powered by NICT】

One-pot synthesis of echinus-like Fe-doped SnO₂ with enhanced photocatalytic activity under simulated sunlight

著者 (6件)： Zhang Jinhua (Department of Chemistry, College of Science, Huazhong Agricultural University, Wuhan 430070, China) ,  Ye Jianfeng (Department of Chemistry, College of Science, Huazhong Agricultural University, Wuhan 430070, China) ,  Chen Hao (Department of Chemistry, College of Science, Huazhong Agricultural University, Wuhan 430070, China) ,  Qu Yang (Department of Chemistry, College of Science, Huazhong Agricultural University, Wuhan 430070, China) ,  Deng Qian (Department of Chemistry, College of Science, Huazhong Agricultural University, Wuhan 430070, China) ,  Lin Zhidong (Provincial Key Laboratory of Plasma Chemistry & Advanced Materials, Wuhan Institute of Technology, Wuhan 430073, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 695  ページ： 3318-3323  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 2 4nmの直径を有する超薄ナノロッドから構成されたユニークなウニ様FeドープSnO_2粒子を,ワンポットソルボサーマル法,塩酸はSnCl_4とFeCl_3の加水分解速度を制御するために用いたによって容易に合成した。調製したままの試料を,透過型電子顕微鏡(TEM),高分解能TEM(HRTEM),X線回折(XRD),およびN_2吸着-脱着分析によって特性化した。得られたウニ様FeドープSnO_2複合材料は,ローダミンB(RhB)の光分解と模擬太陽光照射下でのCr(VI)の光還元,それは主にEg Feドーピング,高い比表面積と構造の多孔性減少に起因すると考えられる反応に対し増強された活性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 六価クロム ,  ナノロッド ,  *光触媒 ,  光還元 ,  透過型電子顕微鏡 ,  *ドーピング ,  比表面積 ,  光分解 ,  *ワンポット合成 ,  多孔性 ,  塩酸
準シソーラス用語： HRTEM ,  ソルボサーマル合成 ,  *光触媒活性 ,  *模擬太陽 , 【Automatic Indexing@JST】

著者キーワード (5件)： SnO_2 ,  Echinus様 ,  Feドープ ,  ソルボサーマル ,  光触媒

分類 (2件)： 光化学一般  (CB08010U) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (7件)： 模擬太陽光 ,  強化 ,  光触媒活性 ,  ウニ ,  Fe ,  ドープ ,  ワンポット合成