熱サイクルと高齢者炭素繊維/ポリイミド積層材における微小亀裂【Powered by NICT】

Microcracking in thermally cycled and aged Carbon fibre/polyimide laminates

著者 (6件)： Zrida H. (Division of Materials Science, Lulea University of Technology, SE-97187 Lulea, Sweden) ,  Zrida H. (Institut Jean Lamour, Ecole Europeenne d’Ingenieurs en Genie des Materiaux, Universite de Lorraine, 6 Rue Bastien Lepage, F-54010 Nancy Cedex, France) ,  Fernberg P. (Division of Materials Science, Lulea University of Technology, SE-97187 Lulea, Sweden) ,  Fernberg P. (Swerea SICOMP AB, SE-941 26 Pitea, Sweden) ,  Ayadi Z. (Institut Jean Lamour, Ecole Europeenne d’Ingenieurs en Genie des Materiaux, Universite de Lorraine, 6 Rue Bastien Lepage, F-54010 Nancy Cedex, France) ,  Varna J. (Division of Materials Science, Lulea University of Technology, SE-97187 Lulea, Sweden)
資料名： International Journal of Fatigue  (International Journal of Fatigue)
巻： 94  号： P1  ページ： 121-130  発行年： 2017年 
JST資料番号： D0802B  ISSN： 0142-1123  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高使用温度のために設計された熱硬化性ポリイミド樹脂を用いた炭素繊維T6508ハーネス朱子織布複合材料は340°Cで凝固した。高熱応力は室温まで冷却後に発生し,それは試験した準等方性複合材料の束における多重亀裂をもたらした。複合材料は二熱サイクルランプを受け,各束の亀裂密度の増加を定量化した。同じ最低温度二ランプの比較は,サイクル内の最高温度は,熱疲れ抵抗に及ぼす顕著な影響を持つことを示した。288°Cでの熱エージング試験中の機械的性質は時間とともに劣化し,ある熟成時間後に亀裂密度を測定した。加齢と疲労効果を解析し,熱サイクル試験における亀裂の一部であるサイクルの高温部中の材料老化に関係していることを示しを別々に行った。数値端応力解析と破壊力学を用いて,観察結果を説明した。三次元有限要素端応力解析は,エッジ上の異なる層の間の損傷状態の大きな差を誘導することを大きなエッジ効果であることを明らかにした。線形弾性破壊力学は内部層と比較して表面層における高い発生・進展亀裂密度を説明した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *積層材料 ,  *熱サイクル ,  破壊力学 ,  熱疲れ ,  *微小亀裂 ,  三次元 ,  熱劣化 ,  高温 ,  複合材料 ,  *炭素繊維 ,  機械的性質 ,  *亀裂 ,  *ポリイミド ,  応力解析
準シソーラス用語： 亀裂密度 , 【Automatic Indexing@JST】

著者キーワード (5件)： 熱疲れ ,  高温特性 ,  熱老化 ,  織物複合材料 ,  破壊力学

分類 (1件)： 金属材料  (HC05020S)

タイトルに関連する用語 (6件)： 熱サイクル ,  高齢者 ,  炭素繊維 ,  ポリイミド ,  積層材 ,  微小亀裂