冷間圧延IF鋼薄板の真の応力制御ラチェット挙動【Powered by NICT】

True stress-control ratcheting behaviour of cold-rolled interstitial-free steel sheet

著者 (7件)： De ParthaSarathi (Metallurgical and Material Engineering Department, Jadavpur University, Kolkata 700032, India) ,  Mahato Jayanta Kumar (Centre of Excellence in Phase Transformation and Product Characterisation (TEQIP-II), India) ,  Kundu Amrita (Metallurgical and Material Engineering Department, Jadavpur University, Kolkata 700032, India) ,  Kundu Amrita (Centre of Excellence in Phase Transformation and Product Characterisation (TEQIP-II), India) ,  Chakraborti P.C. (Metallurgical and Material Engineering Department, Jadavpur University, Kolkata 700032, India) ,  Chakraborti P.C. (Centre of Excellence in Phase Transformation and Product Characterisation (TEQIP-II), India) ,  Shome M. (Research and Development, TATA Steel, Jamshedpur 831007, India)
資料名： Mechanics of Materials  (Mechanics of Materials)
巻： 115  ページ： 34-46  発行年： 2017年 
JST資料番号： E0966A  ISSN： 0167-6636  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 厚さ2.3mmのチタン安定化IF鋼の真応力制御ラチェッティング挙動は,試験片の完全な破壊まで一定最大応力,一定の平均応力と一定応力振幅条件下で調べた。破壊までのラチェッティング歪,および様々なストレス条件下で破壊までのサイクルは,総および正味の繰返し塑性歪応答に対する背応力の発達を考慮することにより説明した。一定最大応力での応力比の増加のために,より高い応力の非対称性は,より低いラチェッティング変形をもたらすことが分かった。これは平均応力支援硬化と低い背応力振幅減少応力振幅から生じたにより起こる。一方,平均応力誘起硬化は,一定応力振幅でラチェッティング疲れ寿命を改善した。一定の平均応力で応力振幅の増加を伴う繰返し塑性歪応答の増幅は高い応力振幅で高いラチェッティング歪蓄積をもたらした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *冷間圧延 ,  *IF鋼 ,  *薄板 ,  非対称性 ,  平均応力 ,  疲れ寿命 ,  応力比 ,  塑性歪 ,  破面検査 ,  チタン
準シソーラス用語： 歪蓄積 ,  応力振幅 ,  最大応力 ,  真応力 , 【Automatic Indexing@JST】

著者キーワード (6件)： IF鋼 ,  真応力 ,  ラチェット疲労 ,  平均応力 ,  応力振幅 ,  フラクトグラフィー