ハイブリッド被覆したFe-Siナノ結晶粉末に基づく軟磁性複合材料【Powered by NICT】

Soft magnetic composites based on hybrid coated Fe-Si nanocrystalline powders

著者 (5件)： Neamtu B.V. (Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca, Romania) ,  Nasui M. (Center for Superconductivity, Spintronics and Surface Science, Technical University of Cluj-Napoca, Memorandumului Street, no 28, 400114 Cluj-Napoca, Romania) ,  Marinca T.F. (Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca, Romania) ,  Popa F. (Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca, Romania) ,  Chicinas I. (Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca, Romania)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 330  ページ： 219-227  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ハイブリッド被覆したナノ結晶Fe-Si粉末に基づく軟磁性複合材料圧粉体の調製と特性化を提示した。Fe-Si粉末を20hまでのFe-Si電気鋼シートの機械的粉砕によって調製した。ハイブリッド被覆は,電気的絶縁性のりん酸塩とFe-Si粒子を被覆している高分子層から構成されている。粒子表面上のりん酸塩処理時間の影響を,SEM,EDX,XRD,及びFTIR研究により調べた。非被覆粉末と比較して,60年代のりん酸塩処理した粉末の飽和磁化は17%と減少した。圧粉体の初期相対透磁率とパワー損失に及ぼす締固め圧力,りん酸塩処理時間,の影響を調べた。圧縮圧力を増加させるコンパクトの透過性とヒステリシス損失の減少の増加につながることが分かった。より短い処理時間はFe-Si粒子のりん酸による部分的被覆し,高透磁率によって特徴づけられるより高い密度を持つ圧粉体をもたらした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： リン酸 ,  *粉体 ,  キャラクタリゼーション ,  X線回折 ,  *複合材料 ,  透磁率 ,  *ナノ結晶 ,  飽和磁化 ,  リン酸塩 ,  鋼板 ,  *被覆 ,  加工時間 ,  圧粉体 ,  リン酸塩処理
準シソーラス用語： メカニカルミリング , 【Automatic Indexing@JST】

著者キーワード (4件)： 軟磁性複合材料 ,  ハイブリッドコーティング ,  りん酸塩処理 ,  ナノ結晶粉末

分類 (1件)： 化成処理  (WC08050J)

タイトルに関連する用語 (6件)： Fe ,  Si ,  ナノ結晶 ,  粉末 ,  軟磁性 ,  複合材料