Ta合金化によるTi_1-xAl_xNの時効硬化の調製

Tailoring age hardening of Ti_1-xAl_xN by Ta alloying

著者 (6件)： Grossmann Birgit (Department Physical Metallurgy and Materials Testing, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria) ,  Jamnig Andreas (Department Physical Metallurgy and Materials Testing, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria) ,  Schalk Nina (Department Physical Metallurgy and Materials Testing, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria) ,  Czettl Christoph (Ceratizit Austria GmbH, Metallwerk-Plansee-Strasse 71, 6600 Reutte, Austria) ,  Pohler Markus (Ceratizit Austria GmbH, Metallwerk-Plansee-Strasse 71, 6600 Reutte, Austria) ,  Mitterer Christian (Department Physical Metallurgy and Materials Testing, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, 8700 Leoben, Austria)
資料名： Journal of Vacuum Science & Technology. A. Vacuum, Surfaces and Films  (Journal of Vacuum Science & Technology. A. Vacuum, Surfaces and Films)
巻： 35  号： 6  ページ： 060604-060604-6  発行年： 2017年11月 
JST資料番号： C0789B  ISSN： 0734-2101  CODEN： JVTAD6  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,0≦y≦0.231の範囲でTa含有量を変化させることによって,アーク蒸着Ti_1-x-yAl_xTa_yNハードコーティングの組織,機械的性質,および熱安定性を系統的に調査した。示差走査熱量測定,および1500°Cまでの真空アニーリング,並びにその後のX線回折分析およびナノインデンテーション測定の組み合わせにより,コーティングの微細構造の変化と,その機械的特性に及ぼす影響についての包括的な洞察を提供した。準安定なTi_1-xAl_xN固溶体へのTaの添加により,スピノーダル分解およびウルツ鉱相形成がより高温にシフトした。その結果,Ta合金コーティングが硬度を維持する温度範囲は1000°Cまで拡張された。(翻訳著者抄録)

シソーラス用語： *タンタル合金 ,  *合金化 ,  アルミニウム化合物 ,  チタン化合物 ,  *時効硬化 ,  イオンめっき ,  *セラミック被覆 ,  *微細構造 ,  *物理的性質 ,  スピノーダル分解 ,  硬度
準シソーラス用語： 窒化アルミニウムチタン ,  アーク蒸着 ,  結晶微細構造 ,  *熱機械的特性

分類 (3件)： 金属材料へのセラミック被覆  (YC02050V) ,  無機化合物の結晶構造一般  (BK07001T) ,  材料試験  (HB02020U)

タイトルに関連する用語 (3件)： Ta合金 ,  時効硬化 ,  調製