β凝固γ-TiAl合金シートの開発【Powered by NICT】

Development of β-solidifying γ-TiAl alloys sheet

著者 (6件)： Zeng Shangwu (Beijing Guowang Fuda Science & Technology Development Co., Ltd., Beijing 100070, China) ,  Zeng Shangwu (Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhao Aimin (Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Luo Lin (Automotive Engineering Product Research & Development Institute, Borgward Automotive Co., Ltd., Beijing 102206, China) ,  Jiang Haitao (Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Zhang Lei (Beijing Guowang Fuda Science & Technology Development Co., Ltd., Beijing 100070, China)
資料名： Materials Letters  (Materials Letters)
巻： 198  ページ： 31-33  発行年： 2017年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： β固化γ-TiAl合金Ti-6.5Al8Nb-1.0Mo-3Si-1B(at.%)シートをホットパック圧延,熱間鍛造,インゴットから直接実施したにより作製した。圧延のままの合金シートのミクロ組織と機械的性質を調べた。圧延のままの合金シートのミクロ組織は5μm~15μmの範囲のサイズを有する微細で均一なガンマに近い微細構造を示した。合金の優れた熱間変形能は(α+γ+β)領域における圧延中の無秩序bccβ相形成とα_2/γラメラコロニー分解の高い体積分率に起因した。圧延したままのシートの改良機械的性質は結晶粒微細化に起因していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： β相 ,  機械的性質 ,  *凝固 ,  圧延 ,  微細構造 ,  *合金 ,  体積率 ,  熱間鍛造 ,  結晶粒微細化 ,  インゴット
準シソーラス用語： 相形成 ,  変形能 ,  *チタンアルミニウム合金 , 【Automatic Indexing@JST】