773K過熱蒸気中で腐食したジルカロイ-4のノジュラ腐食のための新しい機構【Powered by NICT】

A novel mechanism for nodular corrosion of Zircaloy-4 corroded in 773K superheated steam

著者 (8件)： Xie Shijing (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Zhou Bangxin (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Liang Xue (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Liu Wenqing (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Li Hui (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Li Qiang (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Yao Meiyi (Institute of materials, Shanghai University, 200072, Shanghai, China) ,  Zhang Jinlong (Institute of materials, Shanghai University, 200072, Shanghai, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 126  ページ： 44-54  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 773K/10.3MPa過熱水蒸気中のジルカロイ-4板試験片の耐食性は異方性である。圧延表面(S_N)は主に均一腐食を受けるが,横方向(S_T)と圧延方向(S_R)に垂直な表面に垂直な表面は主にノジュラ腐食を受ける。酸化物とマトリックス(O/M)間の界面でのSn偏析に関連したノジュラ腐食の新しい機構を提案した。異方性ノジュラー腐食は異なった木理方向を持つS_N,S_RとS_T表面上に形成されたO/M界面でのSn偏析の異方性から生じた。最後に,ジルコニウム合金のノジュラー腐食に関するいくつかの報告された結果を議論した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ジルコニウム合金 ,  全面腐食 ,  スズ ,  耐食性 ,  *ジルカロイ ,  *過熱蒸気 ,  偏析 ,  異方性 ,  *腐食 ,  酸化物 ,  木理 ,  圧延 ,  界面
準シソーラス用語： *ノジュラー腐食 ,  *ジルカロイ4 , 【Automatic Indexing@JST】

著者キーワード (5件)： ジルカロイ-4 ,  Sn偏析 ,  結節性腐食 ,  Anisotropy ,  三次元原子プローブ

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (4件)： 過熱蒸気 ,  腐食 ,  ジルカロイ-4 ,  ノジュラ腐食