J-GLOBAL ID：201702279824667861   整理番号：17A1058601

珪藻土プレホームの炭素熱還元により作製した大型多孔質Si_3N_4セラミック管の特性【Powered by NICT】

Properties of large-sized porous Si₃N₄ ceramic tubes fabricated by carbothermal reduction of diatomite preforms

著者 (6件)： Li Xiangming (School of Environment and Materials Engineering, Yantai University, Yantai, Shandong 264005, PR China) ,  Li Rui (School of Environment and Materials Engineering, Yantai University, Yantai, Shandong 264005, PR China) ,  Zhu Xiaotao (School of Environment and Materials Engineering, Yantai University, Yantai, Shandong 264005, PR China) ,  Zhou Yanli (School of Environment and Materials Engineering, Yantai University, Yantai, Shandong 264005, PR China) ,  Ren Guina (School of Environment and Materials Engineering, Yantai University, Yantai, Shandong 264005, PR China) ,  Zhang Liang (Sports Medicine Department of Honghui Hospital, Xi’an Jiaotong University Medicine College, Xi’an, Shaanxi 710054, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 13  ページ： 10559-10565  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高多孔性,複雑な形状と大きな次元を持つSi_3N_4セラミックを珪藻土プレホームの炭素熱還元により作製することができた。例として大きな管状多孔質Si_3N_4セラミックを作製し,焼結中の窒素の流れタイプと流量が,管の全体性能にほとんど影響を及ぼさないが,管の異なる位置での組成,間隙率及び曲げ強度に大きく影響する。窒素流速が0.2 1~2.0l/minの範囲にあるとき,通常の焼結により作製したとき管は空隙率73.7 79.6%,10.5 13-1.2MPaの曲げ強さを有し,方向性焼結により作製したとき,空孔度73.2 81.3%,8.6 14 7MPaの曲げ強さを有している。窒素流速が増加すると,通常の焼結により作製した管の異なる位置での組成,気孔率及び曲げ強さは均一になる傾向にあるが,方向性焼結により作製した管の組成,間隙率及び曲げ強度の勾配がより明らかになった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 流速 ,  窒素 ,  *珪藻土 ,  曲げ強さ ,  多孔性 ,  流量 ,  *プリフォーム ,  指向性 ,  *セラミック ,  空隙率 ,  焼結
準シソーラス用語： *セラミック管 ,  *炭素熱還元 , 【Automatic Indexing@JST】

著者キーワード (5件)： Si_3N_4 ,  珪藻土 ,  窒化焼結 ,  多孔質 ,  勾配分布

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (6件)： 珪藻土 ,  プレホーム ,  炭素熱還元 ,  作製 ,  大型 ,  セラミック管