600°C実験とシミュレーションでの鉄の酸化【Powered by NICT】

Oxidation of iron at 600 °C - experiments and simulations

著者 (6件)： Larsson H. (Unit of Structures, Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-10044 Stockholm, Sweden) ,  Jonsson T. (High Temperature Corrosion Centre, Chalmers University of Technology, SE-41296 Goteborg, Sweden) ,  Naraghi R. (Thermo-Calc Software, Norra Stationsgatan 93, SE-11364 Stockholm, Sweden) ,  Gong Y. (Department of Materials, Department of Engineering Science, University of Oxford, Parks Road, Oxford, OX1 3PH, UK) ,  Reed R. C. (Department of Materials, Department of Engineering Science, University of Oxford, Parks Road, Oxford, OX1 3PH, UK) ,  Ågren J. (Unit of Structures, Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-10044 Stockholm, Sweden)
資料名： Materials and Corrosion  (Materials and Corrosion)
巻： 68  号： 2  ページ： 133-142  発行年： 2017年 
JST資料番号： E0386A  ISSN： 0947-5117  CODEN： MTCREQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 純鉄は乾燥O_2(酸素分圧0.05,bal。N_2)で600°Cと1barで酸化し,質量増加のみならず,個々の酸化物相の厚さを測定した。酸化過程はDictraに実装された均質化モデルの修正版を用いてシミュレートされている;これは酸化物スケール形成の動力学と特に形成するヘマタイト(Fe_2O_3),磁鉄鉱(Fe_3O_4),ウスタイト(FeO)の進化を合理的に説明するために役立った。独立評価済みの熱力学的および速度論的Calphadデータベースを計算に必要であるこれらの詳細を与えた。シミュレーション結果と実験データの間に妥当な一致が得られたが,これは酸化速度に及ぼす結晶粒界拡散の大きな影響はさらなる検討を必要とすると結論した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 速度論 ,  酸化物 ,  粒界拡散 ,  磁鉄鉱 ,  *鉄 ,  データベース ,  *酸化 ,  ウスタイト ,  純鉄 ,  *シミュレーション ,  均質化 ,  熱力学 ,  赤鉄鉱
準シソーラス用語： 酸化速度 ,  酸素分圧 , 【Automatic Indexing@JST】

著者キーワード (5件)： Calphad ,  鉄 ,  モデリング ,  oxidation ,  シミュレーション