高温曝露中のチタンとコバルトニッケル基の補修合金のミクロ組織の進展【Powered by NICT】

Microstructural evolution of a titanium- and cobalt-modified nickel-based repair alloy during exposure to high temperatures

著者 (5件)： Liu Xinyu (School of Materials Science & Engineering, Southwest Jiaotong University, Chengdu 610031, China) ,  Xu Yi (School of Materials Science & Engineering, Southwest Jiaotong University, Chengdu 610031, China) ,  Yin Hangboce (School of Materials Science & Engineering, Southwest Jiaotong University, Chengdu 610031, China) ,  Guo Lei (School of Materials Science & Engineering, Southwest Jiaotong University, Chengdu 610031, China) ,  Li Xinggang (National Engineering & Technology Research Center for Nonferrous Metal Matrix Composites, General Research Institute for Nonferrous Metals, Beijing 100088, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 726  ページ： 779-786  発行年： 2017年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： スプレーフォーミング(SF)は広範囲の合金のニアネットシェイプ製造プロセスである。チタンとコバルト修飾修復合金はSFプロセスにより調製し,以前に公表された論文における摩擦と摩耗の優れた特性を示した。本論文では,750°Cで曝露された異なる等温時効時間で合金のミクロ組織の変化を解析した。ミクロ組織観察は,加齢プロセス後か否かインゴット中に形成された等軸結晶粒を明らかにした。サイズとγ′析出物の体積率は時効プロセスの進行中,γ′/γの格子不整合と新しいσ,η相の析出の変化をもたらすと共に増加した。粒界破壊と粒内破壊は時効状態における主な破壊機構である。その引張特性はサイズとエージングプロセス中のγ′析出物,γ′/γ不整合,粒界炭化物と有害相(σおよびη相)の数の体積分率に起因していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *合金 ,  炭化物 ,  η相 ,  体積率 ,  スプレーフォーミング ,  粒界破壊 ,  インゴット ,  時効 ,  粒内破壊 ,  結晶粒 ,  *チタン ,  結晶粒界 ,  *コバルト ,  析出物
準シソーラス用語： 引張特性 , 【Automatic Indexing@JST】

著者キーワード (5件)： スプレーフォーミング ,  γ′析出物 ,  ニッケル基修復合金 ,  σ相 ,  η相

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)