TiO_2/SiO_2塗装の接着の改善のためのアンモニアによる25μmカプトン膜の表面処理【Powered by NICT】

Surface treatment of 25-μm Kapton film by ammonia for improvement of TiO₂/SiO₂ coating’s adhesion

著者 (6件)： Man Yanru (College of Chemistry and Chemical Engineering, Yantai University, Yantai, 264005, China) ,  Li Zhonghua (National Key Laboratory of Vacuum and Cryogenics Technology and Physics, Lanzhou Institute of Physics, Lanzhou, 730000, China) ,  Shu Ming (College of Chemistry and Chemical Engineering, Yantai University, Yantai, 264005, China) ,  Liu Kai (College of Chemistry and Chemical Engineering, Yantai University, Yantai, 264005, China) ,  Liu Huitao (College of Chemistry and Chemical Engineering, Yantai University, Yantai, 264005, China) ,  Gao Yuan (College of Chemistry and Chemical Engineering, Yantai University, Yantai, 264005, China)
資料名： Surface and Interface Analysis  (Surface and Interface Analysis)
巻： 49  号： 9  ページ： 843-849  発行年： 2017年 
JST資料番号： E0709A  ISSN： 0142-2421  CODEN： SIANDQ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Kapton膜の滑らかな疎水性表面のために,その表面上に無機酸化物皮膜を被覆するために非常に困難である。本研究では,カプトンの表面はNH_3H_2Oとシリコンカップリング剤で処理した高分子表面の濡れ性を改善することであった。表面親水性の変化を接触角測定により調べた。試料は接地ベ スのシミュレーションシステムにおいて,原子状酸素(AO)を照射した。TiO_2/SiO_2多層被覆は基材をAO浸食に抵抗するゾル-ゲル法によりKaptonの表面上に作製した。試料の光透過率と表面形態を紫外可視分光法及び走査電子顕微鏡により調べた。結果はTiO_2/SiO_2ゾルは,前処理したKaptonの表面上に一様な薄膜を容易に形成できることを示した。AO露出後,被覆はより緻密になり,剥離はなかった。被覆カプトンのAO腐食生成は急激に低下し,試料は良好な光学的透明性を有していた。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 親水性 ,  前処理 ,  *塗装 ,  接触角 ,  疎水性 ,  *アンモニア ,  酸化膜 ,  ゾル-ゲル法 ,  濡れ ,  走査電子顕微鏡 ,  ケイ素 ,  被覆
準シソーラス用語： 透明性 ,  表面形態 ,  *Kapton , 【Automatic Indexing@JST】

著者キーワード (5件)： Kapton ,  NH3H_2O ,  TiO2/SiO2コーティング ,  原子酸素 ,  ゾル-ゲル

分類 (1件)： 高分子固体のその他の性質  (CG02025L)

タイトルに関連する用語 (4件)： 塗装 ,  アンモニア ,  カプトン ,  表面処理