高容積スーパーキャパシタのためのサンドイッチ構造のポリアニリンナノチューブ/層状グラフェン/ポリアニリンナノチューブ紙の合理的設計【Powered by NICT】

Rational design of sandwiched polyaniline nanotube/layered graphene/polyaniline nanotube papers for high-volumetric supercapacitors

著者 (10件)： Yang Chao (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Zhang Liling (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Hu Nantao (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Yang Zhi (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Su Yanjie (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Xu Shusheng (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Li Ming (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Yao Lu (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Hong Min (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China) ,  Zhang Yafei (Key Laboratory for Thin Film and Microfabrication Technology of the Ministry of Education, School of Electronics, Information and Electrical Engineering, Shanghai Jiao Tong University, Dong Chuan Road No. 800, Shanghai 200240, PR China)
資料名： Chemical Engineering Journal  (Chemical Engineering Journal)
巻： 309  ページ： 89-97  発行年： 2017年 
JST資料番号： D0723A  ISSN： 1385-8947  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： グラフェンベース電極構造の調整と最適化は,携帯型エネルギー貯蔵デバイスのための高い体積および重量容量を達成するために重要である。還元グラフェン酸化物(RGO)-ポリアニリン(PANI)ナノチューブハイブリッド電極の構造を容易に調節され,その場MnO_2ナノワイヤ鋳型重合により合理的に設計した。典型的には,RGO PANI複合材料の二種のアーキテクチャをグラフェン紙におけるMnO_2ナノワイヤの含有量を制御することによって得られた。多孔質RGO PANIナノチューブ紙(0.18mgcm~ 2, 20.0μm)に基づいて組み立てられた対称スーパーキャパシタは,1Ag~( 1)10Ag~から74.3%の優れたレート能力( 1)1Ag~( 1)で956fg~( 1)(単一電極の質量に対して)の高い重量比容量を示した。添加では,サンドイッチされたポリアニリンナノチューブ/層状グラフェン/ポリアニリンナノチューブ紙(0.80mgcm~ 2, 4.02μm)に基づく他の対称素子,単一電極の体積と質量に対する計算した超高体積容量(2A CM~ 3で722fcm~ 3)と相当程度の重量静電容量(1Ag~( 1)で363fg~( 1))を与えた。これらの優れた容量と重量容量性能により,このポリアニリンナノチューブ/層状グラフェン/ポリアニリンナノチューブスーパーキャパシタはその高い体積的および重量性能エネルギー貯蔵のための可能性を有している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 最適化 ,  静電容量 ,  鋳型重合 ,  *サンドイッチ構造 ,  対称性 ,  携帯型 ,  *グラフェン ,  エネルギー貯蔵 ,  ナノワイヤ ,  多孔性
準シソーラス用語： *サンドイッチ ,  比容量 ,  電極構造 ,  *スーパーキャパシタ , 【Automatic Indexing@JST】

著者キーワード (5件)： ポリアニリン ,  グラフェン ,  酸化マンガン ,  体積静電容量 ,  スーパーキャパシタ

分類 (2件)： 吸着,イオン交換  (XD02060I) ,  静電機器  (NB10020R)

タイトルに関連する用語 (6件)： 容積 ,  スーパーキャパシタ ,  サンドイッチ構造 ,  層状 ,  グラフェン ,  設計