CR(3+)ドープTIO_2粉体の化学的沈殿法調製条件を最適化した。【JST・京大機械翻訳】

Preparation optimization of Cr(3+) doped TiO_2 powder by chemical precipitation

著者 (7件)： Zhao Chenxu (Faculty of Materials Science and Engineering, Kunming University of Science and Technology) ,  Du Jinghong (Faculty of Materials Science and Engineering, Kunming University of Science and Technology) ,  Yan Jikang (Faculty of Materials Science and Engineering, Kunming University of Science and Technology) ,  Zhang Jiamin (Faculty of Materials Science and Engineering, Kunming University of Science and Technology) ,  Liu Yichun (Faculty of Materials Science and Engineering, Kunming University of Science and Technology) ,  Gan Guoyou (Faculty of Materials Science and Engineering, Kunming University of Science and Technology) ,  Yi Jianhong (Faculty of Materials Science and Engineering, Kunming University of Science and Technology)
資料名： Gongneng Cailiao  (Gongneng Cailiao)
巻： 47  号： 10  ページ： 10208-10212  発行年： 2016年 
JST資料番号： C2095A  ISSN： 1001-9731  CODEN： GOCAEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： CR(3+)ドープTIO_2粉末を化学的沈殿法により調製し,TIO_2粉末の構造,表面状態及び光吸収特性をXRD,XPS及びUV-VISにより特性化した。結果は,CR(3+)の量がTIO_2粉末の光吸収特性に最も影響し,CR(3+)のドーピング量が増加するとTIO_2の光吸収能力が増加し,バンドギャップが減少することを示した。CR(3+)はTI(4+)を部分的に置換することができ,アナターゼからルチルへの変換を促進し,TIO_2表面にある程度のヒドロキシル基を吸着した。最適調製条件は,CR(3+)の量が1.0%(モル分率),か焼温度が500°C,反応温度が70°C,反応溶液のPH値が10.0であるとき,TIO_2粉末の可視光特性が最も良かった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 光吸収 ,  アナターゼ ,  *粉体 ,  X線回折 ,  ルチル ,  反応温度 ,  キャラクタリゼーション ,  *最適化 ,  可視光 ,  バンドギャップ ,  *ドーピング ,  モル分率 ,  ヒドロキシ基
準シソーラス用語： ヒドロキシル基 ,  か焼温度 ,  *化学的沈殿 , 【Automatic Indexing@JST】

著者キーワード (4件)： titanium dioxide ,  Cr(3+) doping ,  chemical precipitation ,  optimization

分類 (2件)： 光化学反応  (CB08020F) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (6件)： Cr ,  ドープ ,  粉体 ,  化学的沈殿 ,  調製 ,  最適化