アルミナ/イットリアコア-シェル構造の形成によるYAG相の微細構造と相発展に及ぼすTEOSの影響【Powered by NICT】

The effects of TEOS on the microstructure and phase evolutions of YAG phase by formation of alumina/yttria core-shell structures

著者 (4件)： Kafili Golara (Faculty of Advanced Science and Technologies, Department of Nanotechnology Engineering, University of Isfahan, Isfahan, Iran) ,  Loghman-Estarki Mohammad Reza (Department of Materials Engineering, Malek Ashtar University of Technology, Shahin Shahr, Isfahan, Iran) ,  Milani Mostafa (Faculty of Advanced Science and Technologies, Department of Nanotechnology Engineering, University of Isfahan, Isfahan, Iran) ,  Movahedi Behrooz (Faculty of Advanced Science and Technologies, Department of Nanotechnology Engineering, University of Isfahan, Isfahan, Iran)
資料名： Journal of the American Ceramic Society  (Journal of the American Ceramic Society)
巻： 100  号： 9  ページ： 4305-4316  発行年： 2017年 
JST資料番号： C0253A  ISSN： 0002-7820  CODEN： JACTAW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： この研究では,純粋なイットリウムアルミニウムガーネットは,低温での部分化学法により得られた。このアプローチでは,α-アルミナナノ粒子,硝酸イットリウム,尿素,テトラエチルオルトシリケート(TEOS)をAl~3+,Y+~3+,沈殿剤,分散剤及び相形成補助剤としてそれぞれ用いた。結果は分散剤としてTEOS分子は直径200 300nmのアルミナ-イットリアコア-シェル構造のより少ない凝集を引き起こすことを示した,TEOS分子を使用せずに得られた粒子と比較した。さらに,TEOSの0.5及び1wt%を用いて,YAG形成温度は液相拡散機構を通して1400°Cから1200°Cに低下した。このように,この場合,TEOS分子はYAG相の構成のための相形成補助剤として作用した。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *微細構造 ,  αアルミナ ,  沈殿試薬 ,  イットリウムアルミニウムガーネット ,  液相 ,  ナノ粒子 ,  *アルミナ ,  分散剤 ,  低温 ,  凝集 ,  *シェル構造 ,  ウレア化合物
準シソーラス用語： 相形成 ,  硝酸イットリウム ,  化学法 , 【Automatic Indexing@JST】

著者キーワード (4件)： 凝集/凝集体 ,  化学的方法 ,  TEOS ,  YAG

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

物質索引 (1件)： 尿素

タイトルに関連する用語 (7件)： アルミナ ,  イットリア ,  コア-シェル構造 ,  YAG ,  微細構造 ,  発展 ,  TEOS