(TIB_W+TIC_P)/TI複合材料の高温引張挙動と破壊機構を研究した。【JST・京大機械翻訳】

Tensile mechanical behavior and failure mechanism of (TiB_w+TiC_p)/Ti composites at elevated temperature

著者 (6件)： Zhang Changjiang (Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology) ,  Zhang Shuzhi (Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology) ,  Hou Zhaoping (Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology) ,  Lin Peng (Shanxi Key Laboratory of Advanced Magnesium-based Materials, Taiyuan University of Technology) ,  Kong Fantao (National Key Laboratory for Precision Hot Forming of Metals, Harbin Institute of Technology) ,  Chen Yuyong (National Key Laboratory for Precision Hot Forming of Metals, Harbin Institute of Technology)
資料名： Zhongguo Youse Jinshu Xuebao  (Zhongguo Youse Jinshu Xuebao)
巻： 26  号： 11  ページ： 2287-2295  発行年： 2016年 
JST資料番号： W0943A  ISSN： 1004-0609  CODEN： ZYJXFK  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 異なる体積分率(TIB_W+TIC_P)/TI複合材料を真空誘導融解法により調製し,600~750°Cでの高温引張挙動を調べた。結果は以下を示す。(TIB_W+TIC_P)含有量が0から7.5%(体積分率)に増加したとき,(TIB_W+TIC_P)は増加した。TI/TI複合材料は,Β-結晶粒とΑ-シートを著しく微細化した。TIB_WとTIC_PのIN SITU生成は,母材合金の引張強さを増加させ,TIB_W+TIC_Pの体積率の増加とともに増加した。延伸温度の上昇とともに,(TIB_W+TIC_P)は増加した。TI/TI複合材料の引張強さはは%増加し,TIB_WとTIC_Pの強化効果は微細化強化と荷重伝達強化によるものであった。(TIB_W+TIC_P)600°C~700°Cの温度範囲で,TI/TI複合材料の破壊機構は,TIB_WとTIC_Pの破壊が,750°Cでの母材とマトリックスの間の界面剥離であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 延伸 ,  精密化 ,  *複合材料 ,  体積率 ,  合金 ,  *高温 ,  誘導融解 ,  引張強さ ,  結晶粒 ,  温度範囲 ,  荷重伝達 ,  *破壊機構 ,  *引張り挙動 ,  機械的性質 ,  強度
準シソーラス用語： 界面剥離 , 【Automatic Indexing@JST】

著者キーワード (4件)： titanium matrix composite ,  microstructure ,  high temperature tensile property ,  failure mechanism