プロセスローラに及ぼす外部被覆の破壊解析【Powered by NICT】

Failure analysis of the outside coating on the process roller

著者 (5件)： Feng Z.Q. (Key Laboratory of Pressure System and Safety, Ministry of Education, East China University of Science and Technology, Shanghai 200237, China) ,  Wang L. (Baosteel and NSC Automotive Steel Sheets Co., Ltd., Shanghai 200941, China) ,  Wang W.Z. (Key Laboratory of Pressure System and Safety, Ministry of Education, East China University of Science and Technology, Shanghai 200237, China) ,  Cheng K.D. (Key Laboratory of Pressure System and Safety, Ministry of Education, East China University of Science and Technology, Shanghai 200237, China) ,  Chen C.Z. (Key Laboratory of Pressure System and Safety, Ministry of Education, East China University of Science and Technology, Shanghai 200237, China)
資料名： Engineering Failure Analysis  (Engineering Failure Analysis)
巻： 80  ページ： 253-262  発行年： 2017年 
JST資料番号： W0684A  ISSN： 1350-6307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： プロセスローラに及ぼす外部被覆の破壊事例を本研究で提示した。コーティングはWC-Co,高速酸素燃料(HVOF)溶射による45鋼上に堆積している。コーティングのスポーリングがローラの中で見出されている。さび病もローラのコーティングに認められた。被覆の破壊解析は組成分析,およびミクロ組織観察の観点から行った。さらに,サンドブラスト後処理の効果は被覆と基板の間の界面に及ぼす残留砂で比較した。また基板材料の影響を,皮膜の腐食について調べた。基板表面上に残存したサンドブラスト粒子は被覆の破壊に影響を及ぼすと結論した。ローラ上の剥離被覆は酸化鉄の形成とも関連した。空気パージとブラッシングは空気パージと比較してサンドブラスト後使用したときより少ない砂は基板表面上に残存したあるいは無処理を適用した。は,湿式/乾燥循環腐食試験中のWC-Co被覆のための基板として使用されるとき,ステンレス鋼は低炭素鋼よりも優れた耐食性を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *被覆 ,  耐食性 ,  スポーリング ,  腐食試験 ,  ステンレス鋼 ,  界面 ,  溶射 ,  腐食 ,  酸化鉄 ,  低炭素鋼 ,  S45C ,  掃気
準シソーラス用語： サンドブラスティング ,  *破壊解析 ,  *外部被覆 , 【Automatic Indexing@JST】

著者キーワード (4件)： 故障解析 ,  プロセスローラ ,  WC-Co被覆 ,  腐食

分類 (3件)： 熱処理設備  (WC03050A) ,  金属材料  (HC05020S) ,  軸受  (QB01020W)

タイトルに関連する用語 (4件)： プロセス ,  ローラ ,  外部被覆 ,  破壊解析