設計基準外熱条件下での金属と高分子Oリングシールの性能【Powered by NICT】

Performance of metal and polymeric O-ring seals during beyond-design-basis thermal conditions

著者 (6件)： Yang Jiann C. (Fire Research Division, Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA) ,  Hnetkovsky Edward (Fire Research Division, Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA) ,  Rinehart Doris (Fire Research Division, Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA) ,  Fernandez Marco (Fire Research Division, Engineering Laboratory, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA) ,  Gonzalez Felix (U.S. Nuclear Regulatory Commission, Rockville, MD 20852, USA) ,  Borowsky Joseph (U.S. Nuclear Regulatory Commission, Rockville, MD 20852, USA)
資料名： Polymer Testing  (Polymer Testing)
巻： 58  ページ： 135-141  発行年： 2017年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文では,放射性物質輸送パッケージで一般に使用される金属と高分子Oリングシールの性能の小規模熱暴露試験結果を要約した。五つの異なるOリング材料を評価した:Inconel/銀, エチレン-プロピレンジエン単量体(EPDM),ポリテトラフルオロエチレン(PTFE),シリコーン,ブチル,Viton。本研究の全体的な目的は,重度火災による設計基準を越えた温度条件に曝された時,これらのOリングシールの性能試験データと洞察を提供することである。試験は,室温で2bar~5barまでのヘリウムで加圧し小規模ステンレス鋼圧力容器を用いて行った。容器は,予め決められた期間(典型的には8h時間)の900°Cまでの電気炉中で加熱温度にした。圧力降下法は熱暴露中に発生した漏れかどうかを決定するために使用した。実施した46試験のうち,漏れ(容器圧力の損失)は,13回の試験で検出された。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 小規模 ,  加熱温度 ,  火災 ,  ステンレス鋼 ,  曝露試験 ,  圧力損失 ,  温度条件 ,  *Oリング ,  圧力容器 ,  性能試験 ,  放射性物質 ,  ポリシロキサン ,  *設計基準 ,  *密封装置 ,  ヘリウム

著者キーワード (6件)： キャスク ,  輸送パッケージ ,  火災 ,  を越えて設計基準条件 ,  シール ,  使用済燃料

分類 (3件)： 抵抗性  (YH02050K) ,  その他の製品,半製品,利用  (YH06080T) ,  ゴム  (YH07020M)

タイトルに関連する用語 (3件)： 設計基準 ,  高分子 ,  Oリングシール