oligocrystalline Fe Mn Al Ni形状記憶合金ワイヤにおける超弾性に及ぼす繰返し熱処理と加齢の影響【Powered by NICT】

Effects of cyclic heat treatment and aging on superelasticity in oligocrystalline Fe-Mn-Al-Ni shape memory alloy wires

著者 (8件)： Ozcan H. (Department of Mechanical Engineering, Texas A&M University, College Station, TX, USA) ,  Ma Ji (Department of Materials Science and Engineering, Texas A&M University, College Station, TX, USA) ,  Wang S.J. (Department of Materials Science and Engineering, Texas A&M University, College Station, TX, USA) ,  Karaman I. (Department of Mechanical Engineering, Texas A&M University, College Station, TX, USA) ,  Karaman I. (Department of Materials Science and Engineering, Texas A&M University, College Station, TX, USA) ,  Chumlyakov Y. (Siberian Physical Technical Institute, Tomsk 634050, Russia) ,  Brown J. (Dynalloy, Inc., Costa Mesa, CA, USA) ,  Noebe R.D. (NASA Glenn Research Center, Cleveland, OH, USA)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 134  ページ： 66-70  発行年： 2017年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Fe_43 5Mn_34Al_15Ni_7形状記憶合金ワイヤの応力誘起マルテンサイト変態(SIM)に及ぼすナノ析出の影響を調べた。ワイヤ直径比大きな粒径,すなわちオリゴ結晶構造,超弾性を得るために必要であることを示した。室温でSIMと引張強さのための臨界応力は超弾性の損失なしに200°Cでの時効時間と共に増加した。600MPa,および低応力ヒステリシスの高い調整可能な変態応力レベルと,6.7%の超弾性歪は時効したワイヤで得られた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 時効 ,  *熱処理 ,  マルテンサイト変態 ,  結晶構造 ,  *形状記憶合金 ,  ヒステリシス ,  引張強さ ,  *金属線 ,  *超弾性 ,  粒径
準シソーラス用語： 弾性歪 ,  変態応力 ,  臨界応力 ,  ナノ析出 ,  加工誘起マルテンサイト , 【Automatic Indexing@JST】

著者キーワード (5件)： 超弾性 ,  マルテンサイト変態 ,  鉄系形状記憶合金 ,  応力誘起マルテンサイト ,  結晶粒成長

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (9件)： Fe ,  Mn ,  Al ,  Ni ,  形状記憶合金 ,  ワイヤ ,  超弾性 ,  熱処理 ,  加齢