316Lステンレス鋼ナノ/ミクロ二峰性粉末の圧粉と焼結挙動の解析【Powered by NICT】

Analysis of compaction and sintering behavior of 316L stainless steel nano/micro bimodal powder

著者 (4件)： Oh Joo Won (Department of Mechanical Engineering, Pohang University of Science and Technology (POSTECH), 77 Cheongam-Ro, Nam-Gu, Pohang, Gyeongbuk 37673, Republic of Korea) ,  Ryu Seung Kyu (Department of Mechanical Engineering, Pohang University of Science and Technology (POSTECH), 77 Cheongam-Ro, Nam-Gu, Pohang, Gyeongbuk 37673, Republic of Korea) ,  Lee Won Sik (The Advanced Process and Materials R&D Group, Korea Institute of Industrial Technology (KITECH), 156 Gaetbeol-ro, Yeonsu-gu, Incheon 21999, Republic of Korea) ,  Park Seong Jin (Department of Mechanical Engineering, Pohang University of Science and Technology (POSTECH), 77 Cheongam-Ro, Nam-Gu, Pohang, Gyeongbuk 37673, Republic of Korea)
資料名： Powder Technology  (Powder Technology)
巻： 322  ページ： 1-8  発行年： 2017年 
JST資料番号： B0730A  ISSN： 0032-5910  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ナノ粉末を粉末冶金プロセスに及ぼす種々の利点を有していた。しかし,治療におけるその高価格と困難さのために,ナノ粉末は,場に容易に適用することができない。結果として,ナノ/マイクロバイモーダルの粉末の方がこのような問題を克服するために導入した。本研究では,粉末冶金プロセスに及ぼすナノ/ミクロ二峰性粉末中のナノ粉体比の影響を調べた。粒子サイズ双峰分布粉末のためのマスター焼結曲線を初めて開発した。マイクロ,ナノおよび3種類の二峰性粉末を使って,圧密挙動を調べ,膨張焼結は焼結プロセス中の緻密化挙動を解析するために実施した。結果は二峰性粉末は比較的高いグリーン密度を示し,最高値は25%ナノ二峰性粉末で得られたことを示した。粉末は最高の緻密化パラメータを提供した。膨張計データに基づいて,各粉末のマスター焼結曲線を構築し,全ての曲線は,実験データと一致した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 粉末冶金 ,  *粉体 ,  *焼結 ,  圧密 ,  緻密化 ,  粒度 ,  曲線
準シソーラス用語： 膨張計 ,  マスター焼結曲線 ,  二峰分布 ,  ナノ粉末 ,  *SUS316L , 【Automatic Indexing@JST】

著者キーワード (6件)： 二峰性粉末 ,  締固め ,  Dilatometer ,  マスター焼結曲線 ,  ナノ粉末 ,  焼結

分類 (2件)： 圧粉,焼結  (WC02030X) ,  固体の製造・処理一般  (XD03021O)

タイトルに関連する用語 (6件)： 316Lステンレス鋼 ,  粉末 ,  圧粉 ,  焼結 ,  挙動 ,  解析