高温における細粒,炭素結合材料の延性挙動【Powered by NICT】

Ductile behavior of fine-grained, carbon-bonded materials at elevated temperatures

著者 (5件)： Solarek J. (Institute of Materials Engineering, Gustav-Zeuner-Str. 5, Technische Universitaet Bergakademie Freiberg, 09599 Freiberg, Saxony, Germany) ,  Himcinschi C. (Institute of Theoretical Physics, Leipziger Str. 23, Technische Universitaet Bergakademie Freiberg, 09599 Freiberg, Saxony, Germany) ,  Klemm Y. (Institute of Materials Engineering, Gustav-Zeuner-Str. 5, Technische Universitaet Bergakademie Freiberg, 09599 Freiberg, Saxony, Germany) ,  Aneziris C.G. (Institute of Ceramic, Glass and Construction Materials, Agricolastr. 17, Technische Universitaet Bergakademie Freiberg, 09599 Freiberg, Saxony, Germany) ,  Biermann H. (Institute of Materials Engineering, Gustav-Zeuner-Str. 5, Technische Universitaet Bergakademie Freiberg, 09599 Freiberg, Saxony, Germany)
資料名： Carbon  (Carbon)
巻： 122  ページ： 141-149  発行年： 2017年 
JST資料番号： H0270B  ISSN： 0008-6223  CODEN： CRBNA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 炭素結合材料は,高温でそれらのユニークな化学的,物理的および機械的性質のため,耐火物用途に広く用いられている。高温変形の機構は,不明である。本研究では,不活性雰囲気中で1500°Cまでの温度で観察された細粒炭素結合アルミナ及びグラファイト(ISEM 8)の両方の機械的試験からの新しい結果を明らかにした。結果を走査電子顕微鏡による微細構造研究により達成された。Al_2O_3Cに対して,顕著な最大強度対試験温度が1300 1400°Cで生じ,脆性から延性挙動へ変化した。とは対照的に,グラファイトは1500°Cまで強度と延性変形の証拠はないの増加を示した。部品の熱膨張係数の差に基づくモデルをこの現象を説明するために提示した。さらに,Raman分光法は,1500°Cで試験による黒鉛構造の形成を明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *結合材料 ,  高温変形 ,  Raman分光法 ,  走査電子顕微鏡 ,  *延性 ,  脆性 ,  アルミナ ,  *高温 ,  微細構造 ,  グラファイト ,  *炭素 ,  耐火物 ,  熱膨張係数 ,  機械的検査
準シソーラス用語： 延性変形 , 【Automatic Indexing@JST】

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (5件)： 細粒 ,  炭素 ,  結合材料 ,  延性 ,  挙動