模擬セメントモルタル細孔溶液中の球状黒鉛鋳鉄の不動態挙動に関する電気化学的および顕微鏡的研究【Powered by NICT】

Electrochemical and microscopic investigation on passive behavior of ductile iron in simulated cement-mortar pore solution

著者 (5件)： Sun Xiang-Hua (Department of Civil Engineering, Nanjing University of Science and Technology, Nanjing 210094, China) ,  Zuo Xiao-Bao (Department of Civil Engineering, Nanjing University of Science and Technology, Nanjing 210094, China) ,  Yin Guang-Ji (Department of Civil Engineering, Nanjing University of Science and Technology, Nanjing 210094, China) ,  Jiang Kai (Department of Civil Engineering, Nanjing University of Science and Technology, Nanjing 210094, China) ,  Tang Yu-Juan (Department of Civil Engineering, Nanjing University of Science and Technology, Nanjing 210094, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 150  ページ： 703-713  発行年： 2017年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 種々のアルカリ度でシミュレートされたセメントモルタル細孔(SCMP)溶液中の球状黒鉛鋳鉄の不動態挙動を電気化学的測定,開回路電位(OCP),Tafel分極曲線(TP),電気化学インピーダンス分光法(EIS),および顕微鏡試験などにより調べた,走査電子顕微鏡(SEM)とX線光電子分光法(XPS)を含む。結果は,浸漬時間の増加と共に,高いpH値を持つSCMP溶液は球状黒鉛鋳鉄表面のOCPと容量ループ,成長表面膜の形態とその表面酸化鉄化合物中の高いFe~2+/Fe~3+比の増加を引き起こし,球状黒鉛鋳鉄の表面上の不動態膜の形成を呈することを示した。が低いpH値を持つSCMP溶液中で,そのOCP,TP曲線とEISは明らかな変化を示し,低Fe~2+/Fe~3+比を有するさびの腐食形態を生成し,球状黒鉛鋳鉄に及ぼす表面保護の損失を示している。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *不動態 ,  *細孔 ,  *セメントモルタル ,  腐食 ,  *電気化学 ,  鉄化合物 ,  *間隙水 ,  走査電子顕微鏡 ,  電極電位 ,  *球状黒鉛鋳鉄 ,  スペクトロスコピー ,  X線光電子分光法 ,  不動態皮膜
準シソーラス用語： 表面酸化 ,  電気化学インピーダンス分光法 ,  分極曲線 , 【Automatic Indexing@JST】

著者キーワード (5件)： 球状黒鉛鋳鉄 ,  不動態挙動 ,  模擬セメントモルタル細孔溶液 ,  電気化学的測定 ,  SEM/XPS

分類 (2件)： 腐食  (WB03030B) ,  コンクリート構造  (RA04030A)

タイトルに関連する用語 (7件)： セメントモルタル ,  細孔溶液 ,  球状黒鉛鋳鉄 ,  不動態 ,  挙動 ,  電気化学 ,  研究