スーパーキャパシタのための高性能電極材料としての炭素自己修復多孔質g C_3N_4ナノシート/NiCo_2S_4ナノ粒子ハイブリッド複合材料の合成【Powered by NICT】

Synthesis of Carbon Self-Repairing Porous g-C₃N₄ Nanosheets/NiCo₂S₄ Nanoparticles Hybrid Composite as High-Performance Electrode Materials for Supercapacitors

著者 (9件)： Guo Wen (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Wang Jingyu (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Fan Chi (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Chen Zhen (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Liu Peng (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Zhu Dajian (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Xu Zili (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China) ,  Pang Lei (DongFeng Trucks R&D Center, Zhushanhu Road No. 653, Wuhan 430056, PR China) ,  Li Tao (Key Laboratory of Material Chemistry for Energy Conversion and Storage, Ministry of Education, Hubei Key Laboratory of Material Chemistry and Service Failure, School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074, PR China)
資料名： Electrochimica Acta  (Electrochimica Acta)
巻： 253  ページ： 68-77  発行年： 2017年 
JST資料番号： B0535B  ISSN： 0013-4686  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,初めて,高表面積(220.7m~2g~( 1))をもつ炭素自己修復多孔質g C_3N_4ナノシート(CPCN NSs)は,空気中での後の多段階熱処理を結合したソルボサーマル法で調製した。スーパーキャパシタ電極用の炭素自己修復多孔質g C_3N_4ナノシート/NiCo_2S_4ナノ粒子(CPCN NSs/NCS NPs)ハイブリッド複合体を合成するために開発された簡単な水熱法。大きな表面積ならびに超厚さと多孔質構造により,調製したままのCPCN NSsはNiCo_2S_4ナノ粒子(NCS NPs)と結合する優れた足場として役立つ可能性があるが,高伝導率を持つNCS NPは,CPCN NS間の導電性リンカーとして機能し,ハイブリッド複合材料の電気伝導率を改善することができた。電気化学特性評価は,作製したままのハイブリッド複合材料は,優れた電気化学的性質を,高容量(1Ag~( 1)の電流密度で1557fg~( 1))と優れたサイクル安定性(10000サイクル後に7.4%だけの損失)を示すことを示した。これらの結果は,NCS NPとCPCN NSsの組み合わせは,実質的に材料の容量性能を改善し,最終的にスーパーキャパシタ電極のサイクル安定性を増加させることができることを明確に示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 電流密度 ,  *ナノ粒子 ,  表面積 ,  *多孔性 ,  *ナノシート ,  電気伝導率 ,  *電極材料 ,  水熱合成 ,  *ハイブリッド複合材料 ,  導電性
準シソーラス用語： 電気化学的特性 ,  伝導率 ,  ソルボサーマル合成 ,  *自己修復 ,  *スーパーキャパシタ , 【Automatic Indexing@JST】

著者キーワード (4件)： NiCo_2S_4 ,  黒鉛窒化炭素 ,  スーパーキャパシタ ,  エネルギー貯蔵

分類 (1件)： 静電機器  (NB10020R)

タイトルに関連する用語 (8件)： スーパーキャパシタ ,  高性能 ,  電極材料 ,  炭素 ,  自己修復 ,  多孔質 ,  ナノ粒子 ,  ハイブリッド複合材料