強磁性サンドイッチFeCo@graphene@PPyと増強された電磁波吸収特性の合成【Powered by NICT】

Synthesis of ferromagnetic sandwich FeCo@graphene@PPy and enhanced electromagnetic wave absorption properties

著者 (5件)： Wang Yan (School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021, PR China) ,  Wu Xinming (School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021, PR China) ,  Zhang Wenzhi (School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021, PR China) ,  Luo Chunyan (School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021, PR China) ,  Li Jinhua (School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021, PR China)
資料名： Journal of Magnetism and Magnetic Materials  (Journal of Magnetism and Magnetic Materials)
巻： 443  ページ： 358-365  発行年： 2017年 
JST資料番号： H0644A  ISSN： 0304-8853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,FeCo@RGO@PPyの三元サンドイッチ構造を三段階法で作製することに成功した。試料の構造と形態を,XRD,FTIR,XPS,TEM及びFESEMにより特性化した。TEMおよびFESEM画像は,サイズが約20~40nmのFeCo粒子はRGOとPPy間のRGO@PPy,の表面上に成長させたことを示した。VSMの結果はFeCo@RGO@PPy複合材料は強磁性挙動を有し,その電磁波吸収特性を2~18GHzで調べたことを明らかにした。三元複合材料の最大反射損失は4.5GHzで 40.7dBに達することができ, 10dBを超える反射損失の吸収バンド幅は2.5mmの厚さで5.7GHz(3.1から6GHzと12.8 15 10.6GHz),FeCoと比べて改善されたマイクロ波吸収特性を示している。マイクロ波吸収機構も詳細に調べた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *電磁波吸収 ,  キャラクタリゼーション ,  サンドイッチ構造 ,  画像 ,  *強磁性 ,  X線回折 ,  複合材料 ,  吸収バンド
準シソーラス用語： マイクロ波吸収 ,  電界放出型走査電子顕微鏡 ,  *サンドイッチ , 【Automatic Indexing@JST】

著者キーワード (5件)： グラフェン ,  重合体 ,  Nanocomposites ,  磁気特性 ,  マイクロ波吸収

分類 (2件)： 金属結晶の磁性  (BM06040T) ,  磁性材料  (NA04040H)

タイトルに関連する用語 (4件)： 強磁性 ,  サンドイッチ ,  増強 ,  電磁波吸収