熱機械的疲労を受けるシリコン-モリブデン鋳鉄の損傷機構【Powered by NICT】

Damage mechanisms in silicon-molybdenum cast irons subjected to thermo-mechanical fatigue

著者 (5件)： Norman V. (Division of Engineering Materials, Department of Management and Engineering, Linkoping University, SE-58183 Linkoping, Sweden) ,  Skoglund P. (Division of Engineering Materials, Department of Management and Engineering, Linkoping University, SE-58183 Linkoping, Sweden) ,  Skoglund P. (Scania CV AB, Materials Technology, SE-15187 Sodertaelje, Sweden) ,  Leidermark D. (Division of Solid Mechanics, Department of Management and Engineering, Linkoping University, SE-58183 Linkoping, Sweden) ,  Moverare J. (Division of Engineering Materials, Department of Management and Engineering, Linkoping University, SE-58183 Linkoping, Sweden)
資料名： International Journal of Fatigue  (International Journal of Fatigue)
巻： 99  号： P2  ページ： 258-265  発行年： 2017年 
JST資料番号： D0802B  ISSN： 0142-1123  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 熱機械的疲れと組合せ熱機械的および高サイクル疲れ条件下でのシリコン-モリブデン鋳鉄,すなわちEN GJS SiMo5とSiMo1000,アクティブ損傷機構を研究した。研究荷重条件が大型車ディーゼルエンジンの排気マニホールドにおける臨界位置で経験した,すなわち変化全機械的および高サイクル疲れ歪範囲と300 750°Cの温度サイクルである。酸化貫入岩は,巨視的疲れ亀裂は終末期に近い開始される初期生活中に形成されることを確認した。しかし,高サイクル疲れ荷重が重なっている場合,,小亀裂はバルク内の黒鉛ノジュールで優先的に開始した。添加では,表面近くに位置する酸化成長速度と鋳造欠陥の両方が侵入成長に影響を及ぼすことが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： ディーゼル機関 ,  成長速度 ,  酸化 ,  高サイクル疲れ ,  亀裂 ,  鋳造欠陥 ,  グラファイト ,  *鋳鉄 ,  疲れ亀裂 ,  大型車 ,  団塊 ,  熱サイクル
準シソーラス用語： 排気マニホールド ,  *損傷メカニズム ,  *熱機械的疲れ , 【Automatic Indexing@JST】

著者キーワード (5件)： 鋳鉄 ,  熱機械的疲れ ,  高サイクル疲労 ,  環境助長疲れ ,  疲労亀裂成長

分類 (1件)： 金属材料  (HC05020S)

タイトルに関連する用語 (5件)： 熱機械的疲労 ,  シリコン ,  モリブデン ,  鋳鉄 ,  損傷