熱応力解析を用いた部分的に凝固した鉛フリー青銅鋳物の亀裂予測【Powered by NICT】

Crack prediction for a partially solidified lead-free bronze casting using thermal stress analysis

著者 (6件)： Matsushita Akira (Department of Mechanical Engineering, Graduate School of Waseda University, 3-4-1 Shinjuku-ku Okubo, Tokyo 169-8555, Japan) ,  Nakazawa Tomoaki (Department of Mechanical Engineering, Graduate School of Waseda University, 3-4-1 Shinjuku-ku Okubo, Tokyo 169-8555, Japan) ,  Nakazawa Tomoaki (Currently Toyota Motor Corporation, Toyota-cho 1, Toyota-shi, Aichi 471-8571, Japan) ,  Okane Toshimitsu (National Institute of Advanced Industrial Science and Technology, 1-1-1 Tsukuba Umezono, Ibaraki 305-8568, Japan) ,  Yoshida Makoto (Department of Mechanical Engineering, Graduate School of Waseda University, 3-4-1 Shinjuku-ku Okubo, Tokyo 169-8555, Japan) ,  Yoshida Makoto (Kagami Memorial Research Institute for Materials Science and Technology, Waseda University, 2-8-26 Shinjuku-ku Nishiwaseda, Tokyo 169-0051,Japan)
資料名： Journal of Materials Processing Technology  (Journal of Materials Processing Technology)
巻： 249  ページ： 46-56  発行年： 2017年 
JST資料番号： H0650A  ISSN： 0924-0136  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 鉛フリー青銅の永久鋳型鋳造における亀裂予測のために,弾粘塑性と弾塑性熱応力解析を行い,比較して鋳造試験であった。弾粘塑性モデルは,実験で定常状態応力無しのレオロジー特性を決定することができる方法によって構築した。最大偏差主(弾粘塑性解析によってのみ)と静水圧応力は鋳造試験で冷間割れと熱間割れの位置と妥当な一致であった。半固体合金のレオロジー特性を考慮した凝固中及び後の亀裂を予測するために特に重要であることを示唆した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *鋳物 ,  金型鋳造 ,  *凝固 ,  冷間割れ ,  弾粘塑性 ,  *熱応力解析 ,  鋳造 ,  *亀裂 ,  高温割れ ,  弾塑性 ,  *青銅 ,  *予測 ,  鋳造試験
準シソーラス用語： レオロジー特性 ,  *鉛フリー , 【Automatic Indexing@JST】

著者キーワード (6件)： 鋳造 ,  冷間割れ ,  銅 ,  熱間割れ ,  半固体 ,  凝固

分類 (3件)： 金属材料  (HC04020L) ,  機械的性質  (WB02030U) ,  鋳型材料,造型  (WC01020F)

タイトルに関連する用語 (5件)： 熱応力解析 ,  凝固 ,  鉛フリー ,  亀裂 ,  予測