二軸スクリュー押出によるポリ(エチレン2,5-フラノジカルボキシラート)/セルロース複合材料の調製と結晶化挙動【Powered by NICT】

Preparation and crystallization behavior of poly(ethylene 2,5-furandicarboxylate)/cellulose composites by twin screw extrusion

著者 (6件)： Codou Amandine (Universite Cote d’Azur, Institut de Chimie de Nice, UMR CNRS 7272, 06108 Nice Cedex 02, France) ,  Guigo Nathanaeel (Universite Cote d’Azur, Institut de Chimie de Nice, UMR CNRS 7272, 06108 Nice Cedex 02, France) ,  van Berkel Jesper Gabrieel (Universite Cote d’Azur, Institut de Chimie de Nice, UMR CNRS 7272, 06108 Nice Cedex 02, France) ,  van Berkel Jesper Gabrieel (Avantium Chemicals B.V., Zekeringstraat 29, 1014 BV, Amsterdam, The Netherlands) ,  de Jong Ed (Avantium Chemicals B.V., Zekeringstraat 29, 1014 BV, Amsterdam, The Netherlands) ,  Sbirrazzuoli Nicolas (Universite Cote d’Azur, Institut de Chimie de Nice, UMR CNRS 7272, 06108 Nice Cedex 02, France)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 174  ページ： 1026-1033  発行年： 2017年 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ポリ(エチレン2,5 フランジカルボキシラート)(PEF),新たなバイオベースポリエステル,を二軸スクリュー押出によるセルロースと混合した。混合時間,スクリュー速度及び温度のような種々の押出しパラメータを採用した。1 2および4%のセルロースw/wを含む複合薄膜を調製し,比較して純PEF膜であった。PEF/セルロース複合材料の形態を走査電子顕微鏡(SEM)で調べ,押出後の分子量はサイズ排除クロマトグラフィー(SEC)を用いて制御した。PEFの等温及び非等温結晶化に及ぼすセルロースの影響を示差走査熱量測定(DSC)により調べた。結晶化はセルロースが存在すると速くなり,核形成効果はセルロース濃度と共に増加した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 走査電子顕微鏡 ,  示差走査熱量測定 ,  *セルロース ,  分子量 ,  *二軸 ,  *結晶化 ,  混合時間 ,  サイズ排除クロマトグラフィー ,  *複合材料 ,  核形成 ,  薄膜
準シソーラス用語： 非等温結晶化 ,  *結晶化挙動 , 【Automatic Indexing@JST】

著者キーワード (6件)： セルロース ,  ポリ(エチレン25 フランジカルボキシラート) ,  複合材料 ,  結晶化 ,  熱分析 ,  押出