ポリプロピレン繊維を用いたポンピング湿式吹付けコンクリートの配合の研究と最適化【Powered by NICT】

Investigating and optimizing the mix proportion of pumping wet-mix shotcrete with polypropylene fiber

著者 (5件)： Liu Guoming (College of Mining and Safety Engineering, Shandong University of Science and Technology, Qingdao 266590, China) ,  Cheng Weimin (College of Mining and Safety Engineering, Shandong University of Science and Technology, Qingdao 266590, China) ,  Cheng Weimin (State Key Laboratory of Mining Disaster Prevention and Control Co-founded by Shandong Province and the Ministry of Science and Technology, Shandong University of Science and Technology, Qingdao 266590, China) ,  Chen Lianjun (College of Mining and Safety Engineering, Shandong University of Science and Technology, Qingdao 266590, China) ,  Chen Lianjun (State Key Laboratory of Mining Disaster Prevention and Control Co-founded by Shandong Province and the Ministry of Science and Technology, Shandong University of Science and Technology, Qingdao 266590, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 150  ページ： 14-23  発行年： 2017年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 湿式吹付けコンクリートの最適調合を得るために,異なるファイバ長を用いた吹付けコンクリート特性の試験を最初に実施し,切断繊維の状況を統計的に解析した。第二に,湿式吹付けコンクリートの調合要因を田口メソッドを用いて解析した。結果は繊維長は,繊維のせん断および引張破壊を促進することを示した。分散分析(A NOVA)によれば,水/結合剤(W/B)比は,スランプ及び圧縮強度に及ぼす最も効果的なパラメータであったが,ポリプロピレン繊維(PF)は,割裂引張強度及び透水性に及ぼす主要な因子であった。最後に,多因子包括的に考慮した,最終的な配合設計を決定した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 田口メソッド ,  圧縮強さ ,  *ポリプロピレン繊維 ,  *吹付コンクリート ,  分散分析 ,  透水性 ,  *最適化
準シソーラス用語： 配合設計 ,  割裂引張強さ ,  スランプ ,  引張破壊 , 【Automatic Indexing@JST】

著者キーワード (5件)： 湿潤混合吹付けコンクリート ,  ポリプロピレン繊維 ,  繊維切断 ,  田口法 ,  最適配合

分類 (2件)： モルタル,コンクリート  (RA06042H) ,  コンクリート構造  (RA04030A)

タイトルに関連する用語 (5件)： ポリプロピレン繊維 ,  ポンピング ,  配合 ,  研究 ,  最適化