316LN溶接金属の破壊挙動と抵抗性に影響を与える種々の亜結晶粒微細構造【Powered by NICT】

Varied sub-grain microstructure impacts fracture behavior and resistance in 316LN weld metal

著者 (9件)： Keshun Dai (College of Power and Mechanical Engineering, Wuhan University, China) ,  Li Zhu (College of Power and Mechanical Engineering, Wuhan University, China) ,  Wenkai Xiao (College of Power and Mechanical Engineering, Wuhan University, China) ,  Fangyu Chen (Daye Special Steel CO., LTD, China) ,  Fuju Zhang (College of Power and Mechanical Engineering, Wuhan University, China) ,  Xue Yang (College of Power and Mechanical Engineering, Wuhan University, China) ,  Kunqi Mudi (College of Power and Mechanical Engineering, Wuhan University, China) ,  Xian Zhai (College of Power and Mechanical Engineering, Wuhan University, China) ,  Mingxiang Zhang (College of Power and Mechanical Engineering, Wuhan University, China)
資料名： Engineering Fracture Mechanics  (Engineering Fracture Mechanics)
巻： 176  ページ： 100-115  発行年： 2017年 
JST資料番号： A0119A  ISSN： 0013-7944  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： サブグレーン微細構造は一般的に316LN溶接金属(WM)に存在し,亜結晶粒径と形態だけでなく,その方向は変化する。破壊挙動に及ぼす316LN鋳造ミクロ組織特性の影響を解析するために,凝集有限要素法(CFEM)に基づく数値モデルを提示した。実験微細構造画像に基づいて,三種類の形態学的微細構造の定量化パラメータでモデル化した。シミュレーション結果は実験的破壊挙動を良く予測され,これはCFEMモデルの有効性を検証した。二つの破壊モードを要約し,異なる微細構造の破壊抵抗値を定量的に比較し,分析した。溶接金属におけるサブグレーン境界は亀裂伝搬に及ぼす阻害効果を示した。しかし,高体積分率亜粒界の破壊抵抗低下をした。柱状及び樹枝状微細構造は異方性破壊抵抗と長すぎる二次樹枝状晶アーム靭性を悪化させたを示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *微細構造 ,  破壊モード ,  *溶接金属 ,  モルフォロジー ,  結晶粒径 ,  靱性 ,  破壊強さ ,  有限要素法 ,  モデリング ,  鋳造 ,  亀裂伝搬 ,  *亜結晶粒 ,  樹枝状結晶 ,  体積率
準シソーラス用語： *破壊挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： 亜結晶粒 ,  CFEM ,  破壊抵抗 ,  亜結晶粒境界 ,  316LN溶接金属