FV(520)Bステンレス鋼の腐食挙動を,CO_2/H_2S共存下で研究した。【JST・京大機械翻訳】

Corrosion Behavior of FV(520)B Stainless Steel in the Co-existence of CO_2 and H_2S

著者 (8件)： Lang Jingwei (School of Materials Science and Engineering, Hefei University of Technology) ,  Du Xiaodong (School of Materials Science and Engineering, Hefei University of Technology) ,  Jin Shaotong (School of Materials Science and Engineering, Hefei University of Technology) ,  Wang Fucheng (School of Materials Science and Engineering, Hefei University of Technology) ,  Zhan Maji (School of Materials Science and Engineering, Hefei University of Technology) ,  Zhou Dan (School of Materials Science and Engineering, Hefei University of Technology) ,  Shen Jian (School of Materials Science and Engineering, Hefei University of Technology) ,  Liu Guangfu (School of Materials Science and Engineering, Hefei University of Technology)
資料名： Biaomian Jishu  (Biaomian Jishu)
巻： 45  号： 7  ページ： 30-35  発行年： 2016年 
JST資料番号： C2656A  ISSN： 1001-3660  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 【目的】H_2S,H_2O,およびCO_2の条件下で,長距離パイプライン圧縮機(葉)の材料のFV(520)Bの腐食挙動を研究する。方法:H_2S分圧が0.9MPA,CO_2分圧が0.6MPA,温度が150°Cの条件下で,高温高圧反応器を用いて,硫化ナトリウムを調製した。腐食生成物の組成と構造を,XPS,SEM,XRDによって分析した。結果:FV(520)Bステンレス鋼の腐食速度は次第に低下し、サンプルの表面粗さはまず増加し、その後低下し、腐食生成物は主にFECO_3、FE_3O_4、FES、FES_2、S、CR_2S_3、CR_2O_3とCR(OH)_3であった。結論:腐食前期において、FESの形成速度はFES_2、Sより大きく、腐食生成物粒子は絶えず成長している。完全なCR_2O_3とCR(OH)_3保護膜を形成した後,腐食は抑制され,腐食反応は主にFES_2とSの生成であり,試料表面の腐食生成物の粒子サイズは小さくなり,試料の表面粗さは低下した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 高温 ,  X線回折 ,  圧縮機 ,  保護膜 ,  高圧反応器 ,  腐食速度 ,  粒度 ,  硫化ナトリウム ,  *ステンレス鋼 ,  *腐食 ,  分圧 ,  腐食生成物
準シソーラス用語： 長距離 ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： FV(520)B stainless steel ,  sulfidation corrosion ,  hydrogen sulphide ,  carbon dioxide

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (4件)： ステンレス鋼 ,  腐食挙動 ,  共存 ,  研究