柔軟な非対称スーパーキャパシタのためのNドープ多孔性カーボンナノファイバ上へのNi-Co-Sナノシート配列の電着【JST・京大機械翻訳】

Electrodeposition of Ni-Co-S nanosheet arrays on N-doped porous carbon nanofibers for flexible asymmetric supercapacitors

著者 (21件)： Liu Yongkun (National Engineering Laboratory for Textile Fiber Materials and Processing Technology (Zhejiang), Hangzhou 310018, PR China) ,  Liu Yongkun (Key Laboratory of Advanced Textile Materials and Manufacturing Technology (ATMT), Ministry of Education, Hangzhou 310018, PR China) ,  Liu Yongkun (Institute of Smart Fiber Materials, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Lu Qiuling (Department of Polymer Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Huang Zheng (Department of Polymer Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Sun Shiqing (National Engineering Laboratory for Textile Fiber Materials and Processing Technology (Zhejiang), Hangzhou 310018, PR China) ,  Sun Shiqing (Key Laboratory of Advanced Textile Materials and Manufacturing Technology (ATMT), Ministry of Education, Hangzhou 310018, PR China) ,  Sun Shiqing (Institute of Smart Fiber Materials, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Yu Bo (National Engineering Laboratory for Textile Fiber Materials and Processing Technology (Zhejiang), Hangzhou 310018, PR China) ,  Yu Bo (Key Laboratory of Advanced Textile Materials and Manufacturing Technology (ATMT), Ministry of Education, Hangzhou 310018, PR China) ,  Yu Bo (Institute of Smart Fiber Materials, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Evariste Uwamahoro (National Engineering Laboratory for Textile Fiber Materials and Processing Technology (Zhejiang), Hangzhou 310018, PR China) ,  Evariste Uwamahoro (Key Laboratory of Advanced Textile Materials and Manufacturing Technology (ATMT), Ministry of Education, Hangzhou 310018, PR China) ,  Evariste Uwamahoro (Institute of Smart Fiber Materials, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Jiang Guohua (National Engineering Laboratory for Textile Fiber Materials and Processing Technology (Zhejiang), Hangzhou 310018, PR China) ,  Jiang Guohua (Key Laboratory of Advanced Textile Materials and Manufacturing Technology (ATMT), Ministry of Education, Hangzhou 310018, PR China) ,  Jiang Guohua (Institute of Smart Fiber Materials, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Jiang Guohua (Department of Polymer Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, PR China) ,  Yao Juming (National Engineering Laboratory for Textile Fiber Materials and Processing Technology (Zhejiang), Hangzhou 310018, PR China) ,  Yao Juming (Key Laboratory of Advanced Textile Materials and Manufacturing Technology (ATMT), Ministry of Education, Hangzhou 310018, PR China) ,  Yao Juming (Institute of Smart Fiber Materials, Zhejiang Sci-Tech University, Hangzhou 310018, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 762  ページ： 301-311  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,N-ドープ階層的多孔質炭素ナノ繊維(Ni-Co-S@N-pCNFs)上へのNi-Co-S相互接続ナノシート配列の電着により,スーパーキャパシタ用の新しい柔軟性電極材料を調製した。この電極は,電流密度0.2Ag~(-1)と670Fg-1で,2mV・s-1において,550.2Fg-1の顕著な比静電容量を示した。電極としての活性炭(AC)負荷Nドープ多孔性炭素ナノ繊維(AC@N-pCNFs)も調製し,0.2Ag(-1)で257.2Fg(-1)の比静電容量を示し,5000サイクル後に92.6%の静電容量保持で優れたサイクル安定性を示した。さらに,正極としてNi-Co-S@N-pCNFs,負極として活性炭素負荷Nドープ階層的多孔質炭素ナノ繊維(AC@N-pCNFs),電解質とセパレータとしてKOH/NKKハイブリッドを柔軟な非対称スーパーキャパシタに組み立てた。現在のコレクタまたはバインダーを使用しない組み立てスーパーキャパシタデバイスは,134.9W kg(-1)の電力密度で21.6Wh/kg(-1)の高エネルギー密度を示し,1.0Ag(-1)で3000サイクル後に90.0%以上のロバスト長期サイクル安定性を保持した。組み立てられた非対称スーパーキャパシタ(ASCs)は優れた機械的柔軟性と電気化学的安定性を有し,異なる曲げ状態下でのサイクリング中に顕著な減衰は起こらなかった。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アノード ,  粘結剤 ,  活性炭 ,  *電着 ,  柔軟性 ,  静電容量 ,  *ドーピング ,  電流密度 ,  電極材料 ,  カソード ,  *ナノシート ,  *非対称性 ,  *多孔性
準シソーラス用語： 比静電容量 ,  *スーパーキャパシタ , 【Automatic Indexing@JST】

著者キーワード (4件)： 電着 ,  三元ニッケルコバルト硫化物 ,  Nドープ多孔質カーボンナノファイバ ,  スーパーキャパシタ

分類 (1件)： 静電機器  (NB10020R)

タイトルに関連する用語 (8件)： 非対称スーパーキャパシタ ,  ドープ ,  多孔性 ,  カーボンナノファイバ ,  Ni ,  CO ,  ナノシート ,  電着