AEEポリウレタン膜の多重刺激応答性蛍光【JST・京大機械翻訳】

Multi-stimuli-responsive fluorescence of AEE polyurethane films

著者 (4件)： Wang Kun (Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Lu Hao (Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Liu BeiBei (Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Yang Jiping (Key Laboratory of Aerospace Advanced Materials and Performance, Ministry of Education, School of Materials Science and Engineering, Beihang University, Beijing 100191, China)
資料名： European Polymer Journal  (European Polymer Journal)
巻： 101  ページ： 225-232  発行年： 2018年 
JST資料番号： B0690A  ISSN： 0014-3057  CODEN： EUPJA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ソフトセグメントとハードセグメントにそれぞれAIE蛍光体を含むポリウレタンSTMPUとHTMPUを合成し,特性化した。2つの得られたポリウレタン溶液の両方は,凝集強化発光(AEE)特性を示した。次に,2種類のポリウレタン膜を調製し,それらの多重刺激応答特性を探究した。興味深いことに,2つのポリウレタン膜の蛍光発光は高温で減少し,異なる構造のポリウレタンは異なる温度依存性蛍光挙動を有した。一方,アセトンを2つのポリウレタン膜上に滴下すると,弱い発光が得られた。さらに,ポリウレタンSTMPU膜の蛍光は引張応力(ε<0.3)の増加により大きく増強され,多機能蛍光プローブへの応用の可能性を示唆した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 温度依存性 ,  発光 ,  凝集 ,  引張応力 ,  応答特性 ,  キャラクタリゼーション ,  *蛍光 ,  高温 ,  *ポリウレタン ,  *多重化 ,  脂肪族ケトン
準シソーラス用語： 蛍光プローブ ,  蛍光発光 ,  ソフトセグメント ,  *刺激応答 , 【Automatic Indexing@JST】

著者キーワード (5件)： 多重刺激応答特性 ,  メカノフルオロクロミズム ,  ポリウレタン ,  凝集増強発光 ,  テトラアリール-ブタ-13-ジエン