3Y-TZPセラミック上の帯電防止コーティングの調製と特性【JST・京大機械翻訳】

Preparation and properties of anti-static coating on the 3Y-TZP ceramics

著者 (7件)： Yang Xianfeng (College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha 410014, China) ,  Ni Zhentao (College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha 410014, China) ,  Yang Xiaole (College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha 410014, China) ,  He Qinglong (College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha 410014, China) ,  Xie Hehan (College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha 410014, China) ,  Xu Xiewen (College of Materials Science and Engineering, Changsha University of Science & Technology, Changsha 410014, China) ,  Xie Zhipeng (China State Key Laboratory of New Ceramics and Fine Processing, Tsinghua University, Beijing 100084, China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 14  ページ： 16459-16463  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 3Y-TZPセラミック上の帯電防止コーティングを,釉薬にZnOとSnO_2を添加することによって調製した。被覆の濡れ性と表面抵抗を研究した。コーティングにおけるZnOとSnO_2の溶解,結晶化と分布を分析した。被覆の静的散逸機構を調べた。結果は,コーティングと3Y-TZP間の界面結合と濡れが完全であることを示した。被覆の表面抵抗は10~7Ω/□に減少した。ZnOは被覆の濡れ性を改善し,SiO_2の結晶化を抑制するのに役立った。ZnOとSnO_2は釉薬に溶解し,SnO_2周辺の半導電性組成に富む溶融層が形成された。溶融層は互いに接触し,静的散逸ネットワークを確立した。これは被覆の帯電防止特性に起因した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 濡れ ,  界面 ,  半導性 ,  酸化亜鉛 ,  *セラミック ,  *被覆 ,  表面抵抗 ,  ネットワーク ,  表面改質 ,  *帯電防止 ,  結晶化 ,  釉薬
準シソーラス用語： 表面抵抗率 ,  一酸化ケイ素 , 【Automatic Indexing@JST】

著者キーワード (4件)： 帯電防止 ,  表面抵抗率 ,  コーティング ,  表面改質

分類 (1件)： セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： セラミック ,  帯電防止 ,  コーティング ,  調製