文献

J-GLOBAL ID：201802213513644176   整理番号：18A2071655

Cr(VI)吸着のための鉄シートの熱酸化によるヘマタイト(α-Fe_2O_3)ナノ構造の合成【JST・京大機械翻訳】

Synthesis of Hematite (α-Fe₂O₃) Nanostructures by Thermal Oxidation of Iron Sheet for Cr (VI) Adsorption

著者 (4件)： Aquino Christian Laurence E. (University of the Philippines Diliman, Department of Mining, Metallurgical, and Materials Engineering; Philippines) ,  Bongar Mikko James C. (University of the Philippines Diliman, Department of Mining, Metallurgical, and Materials Engineering; Philippines) ,  Silvestre Anfernee B. (University of the Philippines Diliman, Department of Mining, Metallurgical, and Materials Engineering; Philippines) ,  Balela Mary Donnabelle L. (University of the Philippines, Sustainable Electronic Materials Group, Department of Mining, Metallurgical and Materials Engineering; Diliman, Quezon, Philippines, 1101)
資料名： Key Engineering Materials  (Key Engineering Materials)
巻： 775  ページ： 395-401  発行年： 2018年 
JST資料番号： D0744C  ISSN： 1013-9826  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 本研究では,赤鉄鉱(α-Fe_2O_3)ナノ構造を乾燥空気中および水蒸気中でのFeシートの熱酸化により合成した。SEM画像は,ナノシートの表面に成長するナノnanobとナノワイヤを示した。水蒸気中で合成された試料は一般的により大きなナノ構造を生成したが,より高い温度で酸化された試料はより大きなナノ構造を形成した。酸性媒体中のCr(VI)の吸着剤としてα-Fe_2O_3ナノ構造を用いた。クロム除去は,95%の効率で水蒸気中650°Cで合成した試料で最も高かった。速度論的および熱力学的研究は,吸着プロセスが擬二次速度論モデルに強く従い,吸熱性であることを明らかにした。プロセスはLangmuir吸着等温モデルに従い,プロセスが均一で単分子層吸着により記述されることを示唆した。ヘマタイト上へのCr(VI)の吸着は,正に荷電したヘマタイト吸着剤と負のクロムイオンの間の静電反応に起因している可能性がある。Copyright 2018 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： ナノシート ,  ナノワイヤ ,  *ナノ構造 ,  媒質 ,  *吸着 ,  吸着剤 ,  *赤鉄鉱 ,  速度論 ,  単分子層 ,  *六価クロム ,  酸性 ,  熱力学 ,  *熱酸化
準シソーラス用語： クロムイオン ,  クロム除去 , 【Automatic Indexing@JST】

著者キーワード (3件)： 熱酸化 ,  ヘマタイトナノ構造 ,  Cr(VI)吸着

分類 (5件)： 吸着剤  (YB03000W) ,  その他の無機化合物の薄膜  (BK14060A) ,  固体デバイス材料  (NC03020K) ,  塩基,金属酸化物  (CD01030Z) ,  酸化物薄膜  (BK14050P)

タイトルに関連する用語 (6件)： Cr ,  吸着 ,  鉄 ,  熱酸化 ,  ヘマタイト ,  ナノ構造