Dual-functional broadband antireflective and hydrophobic films for solar and optical applications

著者 (5件)： Pendse S. (Centre for Solar Energy Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur PO, Hyderabad 500 005, India) ,  Chandra Sekhar Reddy K. (Centre for Solar Energy Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur PO, Hyderabad 500 005, India) ,  Narendra C. (Centre for Solar Energy Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur PO, Hyderabad 500 005, India) ,  Murugan K. (Centre for Solar Energy Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur PO, Hyderabad 500 005, India) ,  Sakthivel S. (Centre for Solar Energy Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur PO, Hyderabad 500 005, India)
資料名： Solar Energy  (Solar Energy)
巻： 163  ページ： 425-433  発行年： 2018年 
JST資料番号： E0099A  ISSN： 0038-092X  CODEN： SRENA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： メソ多孔性MgF_2ナノ粒子から成る高性能広帯域反射防止(AR)膜の疎水性改質を報告した。MgF_2膜は高い透過率,>99%(400~800nm)および>97%(300~1500nm)を示し,27°の水接触角で親水性であった。簡単なディップコーティングプロセスによるシリカゾルを含むフルオロシランによる疎水性改質は,透過率に影響することなく130°まで水接触角を増加させた。したがって,このハイブリッド層は広い波長範囲(98.8%(400~800nm)と97.03%(300~1500nm))において良好な撥水性と共に優れた反射防止を示した。さらに,この層は環境的にも機械的にも安定で,太陽光および光学応用に適していることを示している。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *広帯域 ,  ナノ粒子 ,  太陽光 ,  親水性 ,  *太陽 ,  *反射防止膜 ,  透過率 ,  *疎水性
準シソーラス用語： 撥水性 ,  波長領域 ,  シリカゾル ,  水接触角 ,  *反射防止 ,  メソポーラス , 【Automatic Indexing@JST】

著者キーワード (6件)： 反射防止 ,  疎水性 ,  ブロードバンド ,  フッ化マグネシウム ,  ナノ粒子層 ,  メソポーラス

分類 (1件)： 太陽電池  (NC03084O)

タイトルに関連する用語 (6件)： 太陽 ,  光学 ,  応用 ,  広帯域 ,  反射防止膜 ,  疎水性膜