High-entropy carbide: A novel class of multicomponent ceramics

著者 (6件)： Zhou Jieyang (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, University of Technology, Wuhan 430070, China) ,  Zhang Jinyong (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, University of Technology, Wuhan 430070, China) ,  Zhang Fan (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, University of Technology, Wuhan 430070, China) ,  Niu Bo (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, University of Technology, Wuhan 430070, China) ,  Lei Liwen (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, University of Technology, Wuhan 430070, China) ,  Wang Weimin (State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, University of Technology, Wuhan 430070, China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 17  ページ： 22014-22018  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,放電プラズマ焼結(SPS)を用いて等原子(Ti,Zr,Hf,Nb,Ta)C高エントロピー炭化物(HEC)粉末を合成し,その相変化,微細構造,組成および酸化挙動を詳細に調べた。結果によると,純粋な面心立方構造固溶体は1950°Cで得られ,金属原子は金属副格子にランダムに配置されていた。結果はまた,HEC粉末がその元の成分より耐酸化性に関してより良い性能を示し,比較的低い温度下で酸化を受けている間に見えない全体として作用することを示した。これは,HEC粉末が元の成分より熱的に安定であることを反映していた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 粉体 ,  相転移 ,  微細構造 ,  放電プラズマ焼結 ,  固溶体 ,  耐酸化性 ,  *炭化物 ,  *セラミック ,  酸化 ,  副格子 ,  *エントロピー
準シソーラス用語： FCC構造 ,  酸化挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： 高エントロピー ,  カーバイド ,  微細構造 ,  組成 ,  酸化

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (3件)： エントロピー ,  炭化物 ,  セラミック