亀裂のあるAl2024-T3及びAl7075-T6板の接着複合材料修理の性能に及ぼす単一引張ピーク過負荷の影響【JST・京大機械翻訳】

Effect of single tensile peak overload on the performance of bonded composite repair of cracked Al 2024-T3 and Al 7075-T6 plates

著者 (5件)： Mohammed Sohail M.A. Khan (Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia) ,  Albedah A. (Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia) ,  Benyahia F. (Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia) ,  Bouiadjra B. Bachir (LMPM, Department of Mechanical Engineering, University of Sidi Bel Abbes, BP 89, Cite Ben M’hidi, Sidi Bel Abbes 22000, Algeria) ,  Bouiadjra B. Bachir (Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Riyadh 11421, Saudi Arabia)
資料名： Composite Structures  (Composite Structures)
巻： 193  ページ： 260-267  発行年： 2018年 
JST資料番号： D0145B  ISSN： 0263-8223  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 実際の作動条件下で,構造は可変およびピーク荷重を受ける。亀裂成長速度は荷重履歴に依存することは良く知られている。過負荷は亀裂成長遅延を発生させるが,低荷重は亀裂成長の加速を生じる。パッチ修復に及ぼす荷重履歴の影響は今までカバーされていない。本研究では,繰返し荷重下で疲れた亀裂Al2024-T3及び7075-T6試料における接着複合材料パッチ修復の性能に及ぼす単一過負荷ピークの影響を実験的に調べた。3つの過負荷ピークの影響を研究した。9,12および14kN,接着複合材料修復の直前および直後に適用した。疲れ寿命と遅延サイクル数は,修復前に試験試料を過負荷に曝すと,亀裂成長の遅延が多くなるが,逆には遅れが少なくなるが,過負荷のみの場合よりも依然として優れていることを示した。過剰荷重を受け,混合モード破壊タイプを観察した破壊試験片の破面を解析するためにSEM観察を行った。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 混合モード ,  *複合材料 ,  破壊試験 ,  破面 ,  疲れ寿命 ,  *亀裂 ,  *接着 ,  *引張 ,  亀裂伝搬 ,  繰返し荷重 ,  *過負荷
準シソーラス用語： 走査電子顕微鏡法 ,  荷重履歴 ,  亀裂伝搬速度 ,  運転条件 , 【Automatic Indexing@JST】

著者キーワード (4件)： 接着複合材料パッチ ,  亀裂修理 ,  過負荷 ,  遅延