ビスフェノールEシアナートエステル樹脂と複合材料の加水分解動力学【JST・京大機械翻訳】

Hydrolytic degradation kinetics of bisphenol E cyanate ester resin and composite

著者 (7件)： Throckmorton James A. (Drexel University Department of Chemical and Biological Engineering, 3141 Chestnut Street, Philadelphia, PA, United States) ,  Feldman Greg (Drexel University Department of Chemical and Biological Engineering, 3141 Chestnut Street, Philadelphia, PA, United States) ,  Palmese Giuseppe R. (Drexel University Department of Chemical and Biological Engineering, 3141 Chestnut Street, Philadelphia, PA, United States) ,  Guenthner Andrew J. (Air Force Research Laboratory, 10 E. Saturn Blvd, Edwards AFB, CA, United States) ,  Lamison Kevin R. (ERC Incorporated, 10 E. Saturn Blvd, Edwards AFB, CA, United States) ,  Redeker Neil D. (ERC Incorporated, 10 E. Saturn Blvd, Edwards AFB, CA, United States) ,  Ruth Patrick N. (ERC Incorporated, 10 E. Saturn Blvd, Edwards AFB, CA, United States)
資料名： Polymer Degradation and Stability  (Polymer Degradation and Stability)
巻： 151  ページ： 1-11  発行年： 2018年 
JST資料番号： E0404B  ISSN： 0141-3910  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： シアナートエステル樹脂系は多くの高温高分子応用に有望であるが,多くの応用に対する可能性は硬化高分子ネットワークの加水分解により制限され,それは樹脂をブリスタし,架橋密度を低下させ,最大許容温度を低下させる。本研究では,ビスフェノールAジシアナートエステル(LECY)とLECYのガラス繊維複合材料の加水分解を調べた。平衡水収着,反応速度,およびガラス転移温度変化をモニターした。拡散と収着の違いにもかかわらず,ガラス繊維複合材料は,劣化の観点から,純粋なポリマーシステムと同様に挙動することが示された。結果をPT-30トリフェノールシアナートエステルと比較し,LECYはより低い平衡水収着値とより低い分解速度を持つことを決定した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 反応速度 ,  *ポリシアヌレート ,  ガラス転移点 ,  収着 ,  架橋度 ,  *複合材料 ,  *加水分解 ,  高温 ,  ガラス繊維 ,  ブリスタリング ,  高分子
準シソーラス用語： 分解速度 ,  水収着 ,  高分子網 , 【Automatic Indexing@JST】

著者キーワード (6件)： 加水分解 ,  ポリシアネート ,  シアナートエステル ,  近赤外線 ,  熱硬化 ,  動力学

分類 (1件)： 高分子の分解,劣化  (CG03010A)

タイトルに関連する用語 (5件)： ビスフェノールE ,  シアナートエステル樹脂 ,  複合材料 ,  加水分解 ,  動力学