NiTi形状記憶合金繊維強化Ti-Al金属金属間化合物積層複合材料の破壊靭性の向上【Powered by NICT】

Improved fracture toughness of NiTi shape memory alloy fiber-reinforced Ti-Al metal-intermetallic-laminate composite

著者 (10件)： Tian Yao (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Wang Enhao (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Li Wei (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Niu Zhongyi (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Chang Yunpeng (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Guo Chunhuan (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Wang Zhenqiang (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Leng Zhe (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China) ,  Leng Zhe (Zhejiang Ocean University, Innovation & Application Institute, Zhoushan, 316022, China) ,  Jiang Fengchun (Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin, 150001, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 739  ページ： 669-677  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本報では,NiTi形状記憶合金繊維なしのTi-Al金属金属間化合物積層(MIL)複合材料の破壊靭性を三点曲げ試験による比較研究を行った。結果は,NiTi形状記憶合金繊維強化(SMAFR)Ti-Al MIL複合材料の破壊靭性はNiTi繊維なしのTi-Al MIL複合材料のそれのほぼ2倍であることを示した。SMAFR MIL複合材料の靭性の改良は,主にNiTi繊維の塑性変形と破壊に起因していた。さらに,NiTi繊維の剥離,金属間化合物層中の主き裂の繰返し曲げ,および金属間化合物の結晶粒微細化は,エネルギーの吸収によるSMAFR MIL複合材料の強靱化に寄与した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *靱性 ,  アルミニウム ,  塑性変形 ,  *破壊靱性 ,  結晶粒微細化 ,  亀裂 ,  *複合材料 ,  *金属間化合物
準シソーラス用語： 強靱化 ,  三点曲げ試験 ,  *積層複合材料 ,  *チタンアルミニウム合金 , 【Automatic Indexing@JST】

著者キーワード (5件)： 積層複合材料 ,  NiTi繊維 ,  金属間化合物 ,  破壊靭性 ,  3点曲げ試験