コバルトナノワイヤの磁気特性に及ぼすサイズ分布の影響【JST・京大機械翻訳】

Effect of size distribution on magnetic properties in cobalt nanowires

著者 (6件)： Xu Huanhuan (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China) ,  Wu Qiong (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China) ,  Yue Ming (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China) ,  Li Chenglin (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China) ,  Li Hongjian (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China) ,  Palaka Subhashini (College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 8  号： 5  ページ： 056422-056422-6  発行年： 2018年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： ソルボサーマル化学プロセスを用いて1,2-ブタンジオール中のCoのカルボン酸塩の還元によりコバルトナノワイヤを合成した。これらのナノワイヤはhcp構造で結晶化し,成長軸は結晶c軸に平行である。反応プロセスの初期段階で機械的撹拌で調製したナノワイヤの形態は,より小さい平均アスペクト比を示したが,狭いサイズ分布を示した。機械的撹拌で調製したナノワイヤの集合は,ほとんど同じ保磁力と残留磁化を示したが,59%の磁気エネルギー積の増加を示した。このエネルギー積の著しい改善は,マイクロ磁気シミュレーションによってさらに理解されている。Coナノワイヤの種々の温度での磁気性能も示した。これらの強磁性ナノワイヤは,高性能で高い熱安定性を有する永久磁石用の新しい理想的なビルディングブロックとなり得る。(翻訳著者抄録)【JST・京大機械翻訳】

シソーラス用語： アスペクト比 ,  結晶化 ,  形態 ,  永久磁石 ,  カルボン酸塩 ,  熱安定性 ,  強磁性 ,  *ナノワイヤ ,  結晶 ,  撹拌 ,  *磁気 ,  残留磁化 ,  保磁力
準シソーラス用語： ビルディングブロック ,  *サイズ分布 , 【Automatic Indexing@JST】