摩擦撹拌溶接7055アルミニウム合金継手のミクロ組織と機械的性質に及ぼす冷却条件の影響【JST・京大機械翻訳】

Effect of cooling conditions on microstructure and mechanical properties of friction stir welded 7055 aluminium alloy joints

著者 (6件)： Lin Huaqiang (School of Materials Science and Engineering, Central South University, Changsha 410083, China) ,  Lin Huaqiang (China CRRC Qingdao Sifang CO., Ltd., National Engineering Technology Research Center for High-speed EMU, Qingdao 266111, China) ,  Wu Yulong (School of Materials Science and Engineering, Central South University, Changsha 410083, China) ,  Liu Shengdan (School of Materials Science and Engineering, Central South University, Changsha 410083, China) ,  Liu Shengdan (Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Center, Changsha 410083, China) ,  Zhou Xiaorong (Corrosion and Protection Centre, School of Materials, The University of Manchester, M13 9PL Manchester, UK)
資料名： Materials Characterization  (Materials Characterization)
巻： 141  ページ： 74-85  発行年： 2018年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 空気冷却および水冷下での摩擦撹拌溶接7075アルミニウム合金の微細構造および機械的性質を,硬度および引張試験,光学顕微鏡および透過型電子顕微鏡によって調査した。水冷却は溶接部の軟化を減少させ,従って空気冷却に比べて高い引張強さをもたらす。破壊は一般的に空気冷却下で溶接された継手の再処理側の熱機械的影響部(TMAZ)と熱影響部(HAZ)内で起こるが,水冷却下で溶接された継手のTMAZとナゲット域(NZ)に向かってシフトする。破面は一般的に空冷継手に対して平坦であるが,水冷継手に対してジグザグ特性を示す。溶接部の機械的挙動を,冷却条件に起因するNZ,TMAZおよびHAZにおける結晶粒構造および析出の変化を考慮して検討した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *摩擦撹拌溶接 ,  透過型電子顕微鏡 ,  折れ線 ,  硬度 ,  微細構造 ,  破面 ,  水冷 ,  引張強さ ,  機械的性質 ,  引張試験 ,  溶接部 ,  結晶粒 ,  *アルミニウム合金 ,  光学顕微鏡 ,  空気冷却

著者キーワード (5件)： 摩擦撹拌溶接 ,  7055アルミニウム合金 ,  冷却条件 ,  微細構造 ,  機械的性質

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 摩擦撹拌溶接 ,  アルミニウム合金 ,  継手 ,  ミクロ組織 ,  機械的性質