Ti/Al多層膜の塑性と破壊挙動の比較研究【JST・京大機械翻訳】

Comparative study on plasticity and fracture behaviour of Ti/Al multilayers

著者 (6件)： Fu Kunkun (Centre for Advanced Materials Technology, School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, NSW 2006, Australia) ,  Sheppard Leigh (School of Computing, Engineering and Mathematics, Western Sydney University, NSW 2751, Australia) ,  Chang Li (Centre for Advanced Materials Technology, School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, NSW 2006, Australia) ,  An Xianghai (Centre for Advanced Materials Technology, School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, NSW 2006, Australia) ,  Yang Chunhui (School of Computing, Engineering and Mathematics, Western Sydney University, NSW 2751, Australia) ,  Ye Lin (Centre for Advanced Materials Technology, School of Aerospace, Mechanical and Mechatronic Engineering, The University of Sydney, NSW 2006, Australia)
資料名： Tribology International  (Tribology International)
巻： 126  ページ： 344-351  発行年： 2018年 
JST資料番号： E0409B  ISSN： 0301-679X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文は,2つの個々の層厚λを有するナノ構造化Ti/Al多層の塑性と破壊挙動に関する比較研究を提示した。ナノインデンテーションの結果は,膜の座屈が10nmの多層で現れ,一方,局在化した剪断帯が100nmの多層で検出されることを示した。ナノ引かきの結果は,局所化した共形亀裂とスポーリングがλ=10nmの多層における支配的な破壊モードであることを示した。一方,臨界垂直荷重に達すると,100nmの多層において接着破壊が観察された。10nm多層膜の接着仕事はλ=10nmのそれよりもはるかに大きく,これはおそらく高硬度と閉じ込められた層機構による転位滑りが少ないためである。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *アルミニウム ,  *多層 ,  剪断帯 ,  ナノインデンテーション ,  接着 ,  亀裂 ,  *多層膜 ,  層厚 ,  ナノ構造 ,  破壊モード ,  *チタン ,  *塑性 ,  スポーリング
準シソーラス用語： 局在化 ,  *破壊挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： ナノ構造Ti/Al多層膜 ,  塑性 ,  破壊 ,  接着の仕事