レーザ粉末層核融合で製造したNi基超合金の熱処理中のδとγ′′の析出と溶解【JST・京大機械翻訳】

Precipitation and dissolution of δ and γ′′ during heat treatment of a laser powder-bed fusion produced Ni-based superalloy

著者 (4件)： Lass Eric A. (Materials Science and Engineering Division, Material Measurement Laboratory, National Institute of Standards and Technology, 100 Bureau Dr., M/S 8555, Gaithersburg, MD, USA) ,  Stoudt Mark R. (Materials Science and Engineering Division, Material Measurement Laboratory, National Institute of Standards and Technology, 100 Bureau Dr., M/S 8555, Gaithersburg, MD, USA) ,  Katz Michael B. (Materials Science and Engineering Division, Material Measurement Laboratory, National Institute of Standards and Technology, 100 Bureau Dr., M/S 8555, Gaithersburg, MD, USA) ,  Williams Maureen E. (Materials Science and Engineering Division, Material Measurement Laboratory, National Institute of Standards and Technology, 100 Bureau Dr., M/S 8555, Gaithersburg, MD, USA)
資料名： Scripta Materialia  (Scripta Materialia)
巻： 154  ページ： 83-86  発行年： 2018年 
JST資料番号： B0915A  ISSN： 1359-6462  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： レーザ粉末層核融合添加剤製造(AM)技術の一つの欠点は,構成板から除去される成分に先立って応力緩和熱処理を必要とする加工中の残留応力の蓄積である。ここでは,870°CでのAMインコネル625の応力緩和焼鈍中に,既知のδ相に沿ったγ′′相の共沈を実証した。AM材料中のγ′′の予想外の析出は,作製したままの凝固ミクロ組織のデンドライト間領域への局所溶質濃縮に起因する。δとγ′′相の溶解は1150°Cで15分間のアニーリング後に達成された。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 応力緩和 ,  凝固 ,  残留応力 ,  焼なまし ,  *熱処理 ,  *溶解 ,  *レーザ ,  ニッケル合金 ,  樹枝状結晶 ,  *核融合 ,  共沈 ,  溶質 ,  δ相 ,  *粉体層
準シソーラス用語： Alloy625 , 【Automatic Indexing@JST】

著者キーワード (3件)： 添加剤製造 ,  Ni基合金 ,  インコネル625

分類 (3件)： 組織的硬化現象  (WB01020C) ,  変態組織,加工組織  (WB01030N) ,  クラッド材  (WE04020G)

タイトルに関連する用語 (7件)： レーザ ,  粉末層 ,  核融合 ,  Ni基超合金 ,  熱処理 ,  析出 ,  溶解