補助セメント材料を組み込んだサンゴ砂コンクリートの耐久性と微細構造【JST・京大機械翻訳】

Durability and microstructure of coral sand concrete incorporating supplementary cementitious materials

著者 (6件)： Cheng Shukai (State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China) ,  Shui Zhonghe (State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China) ,  Sun Tao (State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China) ,  Sun Tao (Key Laboratory of Roadway Bridge & Structure Engineering, Wuhan University of Technology, Wuhan 430070, China) ,  Yu Rui (State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430070, China) ,  Zhang Guozhi (CCCC Second Harbor Engineering Company Ltd., Wuhan 430070, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 171  ページ： 44-53  発行年： 2018年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文は,河川砂コンクリート(RSC)と比較して,多孔性サンゴ砂骨材と補助セメント質材料(SCMs)を使用することによって,サンゴ砂コンクリート(CSC)生産の耐久性性能を調査した。CSCの耐久性特性を,塩化物浸透,水吸収,乾燥収縮,加速炭酸化,および硫酸塩乾燥-湿潤サイクルの観点から評価した。結果は,CSCがRSCと比較して,より高い乾燥収縮,毛管吸水,炭酸化深さ,およびわずかに低い後の圧縮強度を示したことを示した。しかし,多孔質サンゴ凝集体は,その内部硬化により,RSCよりも,より急速な初期強度,塩化物イオン浸透へのより良い抵抗,および硫酸塩乾燥-湿潤サイクルを提供した。さらに,内部硬化とポゾラン反応の組合せはCSCの微細構造改善に寄与し,それはSCMsを含むCSCの良好な耐久性特性に適合した。さらに,生態学的評価は,SCMsのCSC取り込みがCO2放出の有意な減少をもたらすことを示した。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *コンクリート ,  *耐久性 ,  *微細構造 ,  浸透 ,  凝集体 ,  硫酸塩 ,  骨材 ,  湿潤 ,  ポゾラン反応 ,  炭酸化 ,  乾燥収縮 ,  吸水 ,  圧縮強さ
準シソーラス用語： 塩化物イオン ,  *セメント系材料 , 【Automatic Indexing@JST】

著者キーワード (5件)： サンゴ砂骨材 ,  補助セメント材料 ,  耐久性 ,  微細構造 ,  内部硬化

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (4件)： セメント材料 ,  サンゴ砂 ,  コンクリートの耐久性 ,  微細構造