相応力と超塑性の関係を制御することによる微細閉孔を含む軽量アルミナの作製:実験的および数学的研究【JST・京大機械翻訳】

Fabrication of lightweight alumina containing fine closed pores by controlling the relationship between phase stress and superplasticity: Experimental and mathematical studies

著者 (4件)： Fu Lvping (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081, China) ,  Huang Ao (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081, China) ,  Gu Huazhi (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081, China) ,  Ni Hongwei (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, Hubei 430081, China)
資料名： Ceramics International  (Ceramics International)
巻： 44  号： 16  ページ： 20034-20042  発行年： 2018年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究は,微細な閉鎖細孔構造を有する多孔質材料を製造することを目的とした。本研究では,結晶粒界の移動を増加させるために,アルミナ-ゾルおよびCaO微粉末を焼結前にマイクロ-アルミナ粉末に添加した。数学モデルを提案し,誘起相応力を計算し,応力と超塑性の間の関係の定量的記述を提供した。作製した軽量アルミナ試料の特性と微細構造に及ぼす応力と超塑性の関係の影響を調べた。CaO微粉末の添加によって,CaOとAl_2O_3の間の反応は,相応力を生み出し,そしてそれは,アルミナ-ゾルの超塑性を活性化し,そして,結晶粒界移動を増加させることができた。細孔は閉鎖され,移動中に分割される;したがって,試料の閉鎖気孔率は徐々に増加し,一方,開放気孔率と細孔径は減少した。しかしながら,過剰なCaO含有量は結晶粒界の破壊をもたらし,閉じた気孔率を減少させ,開放気孔率を増加させる。本研究における結果によると,約21.14MPaの相応力が,低い開放気孔率,高い閉鎖気孔率,および小さい細孔径を有する軽量アルミナを製造するために製造されるべきである。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 多孔性 ,  多孔質体 ,  焼結 ,  細孔 ,  *アルミナ ,  細孔構造 ,  数学モデル ,  結晶粒界 ,  空隙率 ,  微細構造 ,  *超塑性 ,  細孔径 ,  微粉体
準シソーラス用語： 開放気孔率 ,  *軽量 , 【Automatic Indexing@JST】

著者キーワード (5件)： アルミナ ,  多孔性 ,  ストレス ,  超塑性 ,  微細構造

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (7件)： 超塑性 ,  軽量 ,  アルミナ ,  作製 ,  実験 ,  数学 ,  研究