連続鋳造の際のIF鋼中のマクロ介在物の形成と発現

Formation and evolution of macro inclusions in IF steels during continuous casting

著者 (13件)： DENG Xiaoxuan (Shougang Res. Inst. of Technol., Beijing, CHN) ,  DENG Xiaoxuan (Beijing Key Lab. of Green Recyclable Process for Iron & steel Production Technol., Beijing, CHN) ,  JI Chenxi (Shougang Res. Inst. of Technol., Beijing, CHN) ,  JI Chenxi (Beijing Key Lab. of Green Recyclable Process for Iron & steel Production Technol., Beijing, CHN) ,  CUI Yang (Shougang Res. Inst. of Technol., Beijing, CHN) ,  CUI Yang (Beijing Key Lab. of Green Recyclable Process for Iron & steel Production Technol., Beijing, CHN) ,  TIAN Zhihong (Shougang Res. Inst. of Technol., Beijing, CHN) ,  TIAN Zhihong (Beijing Key Lab. of Green Recyclable Process for Iron & steel Production Technol., Beijing, CHN) ,  YIN Xue (Univ. Sci. and Technol. Beijing, Beijing, CHN) ,  SHAO Xiaojing (Shougang Res. Inst. of Technol., Beijing, CHN) ,  SHAO Xiaojing (Beijing Key Lab. of Green Recyclable Process for Iron & steel Production Technol., Beijing, CHN) ,  YANG Yindong (Univ. Toronto, Ontario, CAN) ,  MCLEAN Alex (Univ. Toronto, Ontario, CAN)
資料名： Ironmaking & Steelmaking  (Ironmaking & Steelmaking)
巻： 44  号： 10  ページ： 739-749  発行年： 2017年 
JST資料番号： C0314B  ISSN： 0301-9233  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： IF鋼は高強度鋼として大きな役割を果たしているが,その製造で用いられる連続鋳造においてはマクロな非金属介在物の生成が製品の表面品質を損なう問題がある。本研究においては,その抑制のための方案の開発に資するために,連続鋳造プロセスの上流(タンディッシュ)からスラブまでの広範囲にわたって,非金属介在物生成の実態を調べた。種々の場所からサンプルを採取し,Aspexによる分析(形態,サイズ,化学組成,数密度)を行なった。この実験から,6種類の形態の5μm以上の大きさの非金属介在物が生成していることを確認し,化学組成は主にアルミナでありAl-Ti複合酸化物も含まれていることを見出した。これらの生成機構は連続鋳造機のノズルの耐火物に由来するものであるが,タンディッシュ内で生成する複合酸化物の生成・成長機構についても論じた。

シソーラス用語： *IF鋼 ,  *連続鋳造 ,  *非金属介在物 ,  耐火物 ,  酸化物 ,  機構
準シソーラス用語： 生成機構 ,  複合酸化物

分類 (2件)： 鋳造欠陥  (WC01060X) ,  その他の金属組織学  (WB01040Y)

タイトルに関連する用語 (5件)： 連続鋳造 ,  IF鋼 ,  マクロ ,  介在物 ,  発現