コークスドラムクラッドの溶接肉盛の熱影響部におけるJagged割れ【Powered by NICT】

Jagged cracking in the heat-affected zone of weld overlay on coke drum cladding

著者 (7件)： Wang Yiyu (Department of Chemical and Materials Engineering, University of Alberta, Edmonton, Alberta T6G 2V4, Canada) ,  Kannan Rangasayee (Department of Chemical and Materials Engineering, University of Alberta, Edmonton, Alberta T6G 2V4, Canada) ,  Li Leijun (Department of Chemical and Materials Engineering, University of Alberta, Edmonton, Alberta T6G 2V4, Canada) ,  Suzuk Yasin (Suncor Energy Inc., Calgary, Alberta T2P 3E3, Canada) ,  Ting Darren (Suncor Energy Inc., Calgary, Alberta T2P 3E3, Canada) ,  Yuen Simon (Suncor Energy Inc., Calgary, Alberta T2P 3E3, Canada) ,  Garcia Maria (Suncor Energy Inc., Calgary, Alberta T2P 3E3, Canada)
資料名： Engineering Failure Analysis  (Engineering Failure Analysis)
巻： 85  ページ： 14-25  発行年： 2018年 
JST資料番号： W0684A  ISSN： 1350-6307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Jagged亀裂はインコネル625オーバレイ修理コークスドラムのSA240 405型ステンレス鋼クラッドで観察された。粒界割れはボート試料の細粒熱影響部(FGHAZ)における支配的破壊モードであることが分かった。手術と溶接熱サイクルからの増感効果は粒界に沿ってCrリッチM_23C_6炭化物の優先的析出によるCrの減少につながった。クラッドFGHAZはより高い局所歪レベルを有する結晶粒界の最大周波数と粒界CrリッチM_23C_6炭化物の最も高い割合を有していた。有限要素解析により予測された熱応力分布は亀裂領域近傍の典型的な「ぎざぎざ」パターンを示すこと最大せん断応力を明確に示した。シェル母材,外装材,及びオーバレイ間の熱膨張係数と強さの不整合は,インコネル625被覆層のクラッディングHAZにおけるユニークなギザギザの最大せん断応力分布の原因となっていると考えられている。この熱応力の大きさは,900°F(482°C)使用温度は感作HAZにおけるギザギザの亀裂形成のための駆動力を提供するでクラッドの降伏強さに達することができた。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 結晶粒界 ,  *溶接 ,  熱膨張係数 ,  粒界割れ ,  ステンレス鋼 ,  熱応力 ,  炭化物 ,  被覆層 ,  破壊モード ,  降伏強さ ,  クロム ,  *肉盛
準シソーラス用語： 有限要素解析 ,  *クラッド層 ,  Alloy625 , 【Automatic Indexing@JST】

著者キーワード (5件)： Jagged割れ ,  熱影響部感作 ,  コークスドラム ,  オーバレイ修復 ,  ステンレス鋼クラッディング

分類 (1件)： 配管材料,弁  (QD05020E)

タイトルに関連する用語 (3件)： 溶接 ,  肉盛 ,  熱影響部