超微細粒Ni-Mo合金における焼なまし誘起硬化【JST・京大機械翻訳】

Annealing-Induced Hardening in Ultrafine-Grained Ni-Mo Alloys

著者 (6件)： Gubicza Jenoe (Department of Materials Physics, Eotvos Lorand University, P.O.B.32, Budapest, H-1518, Hungary) ,  Pereira Pedro Henrique R. (Materials Research Group, Faculty of Engineering and the Environment, University of Southampton, Southampton SO171BJ, UK) ,  Kapoor Garima (Department of Materials Physics, Eotvos Lorand University, P.O.B.32, Budapest, H-1518, Hungary) ,  Huang Yi (Materials Research Group, Faculty of Engineering and the Environment, University of Southampton, Southampton SO171BJ, UK) ,  Vadlamani Subramanya Sarma (Department of Metallurgical and Materials Engineering, Indian Institute of Technology Madras, Chennai 600036, India) ,  Langdon Terence G. (Materials Research Group, Faculty of Engineering and the Environment, University of Southampton, Southampton SO171BJ, UK)
資料名： Advanced Engineering Materials  (Advanced Engineering Materials)
巻： 20  号： 9  ページ： e1800184  発行年： 2018年 
JST資料番号： W2018A  ISSN： 1438-1656  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 超微細粒(UFG)Niにおける焼鈍誘起硬化に及ぼすMo合金化の影響を研究した。低温アニーリング後に観察された硬化は,移動転位の消滅と残留転位の低エネルギー配置への同時クラスタ化によって説明される。Mo濃度の増加と共に,Mo溶質原子が転位の消滅と転位を妨げるので,硬化効果は減少することを本研究は明らかにした。この傾向は,電着Ni-Mo合金で観察されたものと反対であり,そこでは,より大きな合金元素濃度が,より高いアニーリング誘起強化効果をもたらす。この違いはUFGとナノ結晶Ni-Mo合金の異なる変形機構に起因する。Copyright 2018 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  *焼なまし ,  低温 ,  電着 ,  *モリブデン ,  *モリブデン合金 ,  合金元素 ,  クラスタ化 ,  *超微粒子 ,  ナノ結晶
準シソーラス用語： 低エネルギー ,  変形機構 ,  溶質原子 , 【Automatic Indexing@JST】

著者キーワード (5件)： アニーリング ,  転位 ,  硬化 ,  Ni-Mo合金 ,  超微細粒微細構造