J-GLOBAL ID：201802228434907357   整理番号：18A1802721

ZrとSbを組み合わせたAl-20Mg_2Si合金のミクロ組織と摩耗挙動【JST・京大機械翻訳】

Microstructure and wear behaviour of Al-20Mg₂Si alloy with combined Zr and Sb additions

著者 (12件)： Zhu Jia-Ning (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Zhou Ting-Ting (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Zha Min (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Zha Min (International Center of Future Science, Jilin University, Changchun 130012, PR China) ,  Li Chao (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Li Jie-Hua (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Li Jie-Hua (Institute of Casting Research, University of Leoben, Leoben, Austria) ,  Wang Cheng (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Gao Cheng-Long (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Wang Hui-Yuan (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China) ,  Wang Hui-Yuan (International Center of Future Science, Jilin University, Changchun 130012, PR China) ,  Jiang Qi-Chuan (Key Laboratory of Automobile Materials of Ministry of Education, School of Materials Science and Engineering, Nanling Campus, Jilin University, No. 5988 Renmin Street, Changchun 130025, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 767  ページ： 1109-1116  発行年： 2018年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Al-20Mg_2Si合金中の一次Mg_2Siを微細化し,改質するために,ZrとSbを同時に添加した。ZrまたはSbの単一添加と比較して,ZrとSbの組合せ添加は,一次Mg_2Siに及ぼす強化された微細化および改質効果をもたらすことができた。ユニークな共修飾効果は主にSbとZrの相乗的組合せに由来する。SbはMg_3(Sb,Si)_2粒子の形成に関与し,それにより一次Mg_2Siの不均一核として作用し,一次Mg_2Si結晶の均一分布と微細化粒子サイズをもたらす。Zrの役割もまた,それが一次Mg_2Si相の凝固温度間隔を減少させることができるので不可欠であり,それはさらに一次Mg_2Si結晶を微細化して,それらの完全な成長を促進することができた。さらに,Al-20Mg_2Si合金の耐摩耗性は,ZrとSbの特別な共改質効果により改善された。一次Mg_2Siは,不均一核形成を強化し,凝固温度間隔を減少させることにより最適化できるので,他の合金系における微細構造制御を導くために,このようなアイデアを拡張することができる。Copyright 2018 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 凝固点 ,  粒度 ,  *ジルコニウム ,  *金属組織 ,  *アンチモン ,  精密化 ,  *ケイ素合金 ,  アルミニウム ,  微細構造 ,  最適化 ,  *合金 ,  耐摩耗性
準シソーラス用語： 不均一核形成 ,  一様分布 ,  改善効果 ,  *摩耗挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： 改質 ,  一次Mg_2Si ,  不均一核形成 ,  Al-Mg-Si合金

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： Zr ,  Sb ,  Al ,  ミクロ組織 ,  摩耗挙動